Influência de agentes adesivos, irradiação por microondas e ciclagem termomecânica na resistência de união entre uma resina acrílica termoativada e um reembasador rígido

Página do item simplificado
dc.contributor.advisorJunior, Tarcisio José de Arruda Paes [UNESP]
dc.contributor.authorCavalcanti, Sâmia Carolina Mota [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:28:57Z
dc.date.available2014-06-11T19:28:57Z
dc.date.issued2012-07-04
dc.description.abstractEste trabalho tem como objetivo analisar a resistência de união entre uma resina acrílica ativada térmicamente (Vipiwave) e um reembasador rígido (Tokuyama rebase fast II) considerando-se fatores que possam influenciar nesta união, tais como: agentes adesivos, irradiação por micro-ondas e ciclagem termomecânica. Para a execução da pesquisa estabeleceram-se 16 grupos (n=10), para qual foram confeccionados corpos de prova em formato cilíndrico(13mmx23mm) em resina acrílica termoativada em forno de micro-ondas. Após a polimerização, estes receberam acabamento com lixa d’agua 400 e tiveram suas superfícies tratadas com Tokuyama Rebase II adhesive, adesivo Palabond ou o monômero da resina Vipiwave, e reembasados. Uma parte dos corpos de prova foi tratado em micro-ondas, sendo imersos em 200ml de água, e submetidos a um ciclo de 3 min a 650W. Outros grupos foram levadosa ciclagem termomecânica, onde o estresse mecânico foi de 10.000 ciclos a 3,8 Hz. Todos os corpos de prova foram submetidos ao teste de cisalhamento, com velocidade de 1mm/min e carga de 100Kgf em máquina de ensaios universal. Os corpos de prova passaram em avaliação por perfilometria. Após obtenção dos resultados, estes foram submetidos a análise estatística por Anova e Tukey (5%) para comparação entre os grupos. Verificou-se que tanto a irradiação em micro-ondas quanto a ciclagem termomecânica melhoraram significativamente a união nos grupos tratados com Palabond. Os grupos Tokuso e controle apresentaram melhor resistência adesiva após a ciclagem embora o grupo controle apresentasse os piores valores de resistência em todas as situações. Já os resultados de perfilometria mostraram que o adesivo Palabond criou uma superfície mais rugosa (Ra=185,4 m) quando comparado ao grupo Tokuso (Ra= 121,9 m). Concluiu-se desta...pt
dc.description.abstractThe aim of this study was to analyze the shear bond strength between a heat-activated acrylic resin (Vipiwave) and a soft liner (Tokuyama Rebase Fast II) considering factors that can influence bonding, such as adhesive agents, microwave irradiation and thermomechanical cycling. Sixteen groups (n=10) were stablished, and specimens of heat-activated acrylic resin were fabricated in a cylindrical shape (13mmx23mm) in microwave oven. After curing, they were finished with #400 sandpaper, the bonded surfaces were treated with Tokuyama Rebase II adhesive, Palabond or Vipiwave monomer, and were relined with Tokuyama Rebase Fast II. Half of specimens were microwave-cured (3 minutes at 650W). Remainder were heat-cured in water. Half of specimens were thermomechanical cycled (10,000 cycles at 3.8 Hz). Specimens were submitted shear bond strength test with crosshead speed of 1mm/min in a universal testing machine. Fractured specimens were evaluated in profilometry. Data (MPa) were submitted to 3-way ANOVA and Tukey test, both with =0.05 for comparison between groups. Microwave-cured and thermamechanical cycled Palabond treated groups showed higher bond strength. Untreated groups showed the lowest shear bond strengths and the groups treated with Tokuyama adhesive the highest bond strength values. Profilometry showed that Palabond created a rougher surface (Ra = 185.4 m) compared to Tokuso (Ra = 121.9 m). It was concluded that the surface treatment prior to relining, especially with Palabond produces satisfactory results, and microwave irradiation and thermomechanical cycling showed improvement of bond strengthen
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.format.extent84 f. : il.
dc.identifier.aleph000700623
dc.identifier.capes33004145070P8
dc.identifier.citationCAVALCANTI, Sâmia Carolina Mota. Influência de agentes adesivos, irradiação por microondas e ciclagem termomecânica na resistência de união entre uma resina acrílica termoativada e um reembasador rígido. 2012. 84 f. Dissertação ( mestrado) - Uiversidade Estadual Paulista, Faculdade de odontologia de São José dos Campos, 2012.
dc.identifier.filecavalcanti_scm_me_sjc.pdf
dc.identifier.urihttp://hdl.handle.net/11449/97353
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectResinas acrilicaspt
dc.subjectResistência ao cisalhamentopt
dc.subjectPrótese dentáriapt
dc.subjectOdontologia - Aspectos estéticospt
dc.titleInfluência de agentes adesivos, irradiação por microondas e ciclagem termomecânica na resistência de união entre uma resina acrílica termoativada e um reembasador rígidopt
dc.typeDissertação de mestrado
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaImplantes Ósseo-Integradospt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
cavalcanti_scm_me_sjc.pdf
Tamanho:
1.09 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Dissertações - Odontologia Restauradora - ICT