Otimização do processo de deposição de filmes TiO2:Mn usando RF magnetron sputtering

dc.contributor.advisorSilva, José Humberto Dias da [UNESP]
dc.contributor.advisorLisboa Filho, Paulo Noronha [UNESP]
dc.contributor.authorPereira, Andre Luis de Jesus [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:35:45Z
dc.date.available2014-06-11T19:35:45Z
dc.date.issued2012-08-09
dc.description.abstractA busca por um melhor entendimento da inter-relação entre os parâmetros envolvidos no processo de crescimento de filmes de dióxido de titânio (Tio2) e as propriedades estruturais, eletrônicas e magnéticas resultantes foi a principal motivação deste trabalho. Para isso, filmes Ti)2 foram crescidos usando a técnica de RF magnetron sputtering em diferentes condições. Um primeiro conjunto de filmes de Ti)2 não dopados foi depositado com fluxo contínuo de O2. Em outro conjunto, utilizou-se sistemáticas interrupções no fluxo de O2 durante a deposição. O último grupo de amostras foi depositado usando fluxo contínuo O2 e dopagem com Mn. Os filmes do primeiro grupo apresentaram morfologia colunar com estrutura majoritariamente anatase e com gap óptico de ~3,3 eV, independente da temperatura dos substratos (450ºC e 600ºC) e da razão Ar/O2 utilizada. A diminuição do fluxo de O2 provocou um aumento da absorção sub-gap que foi associada a um aumento dos defeitos eletrônicos no material. Um tratamento térmico em vácuo a 800ºC, realizado sobre filmes de TiO2 puros, revelou um aumento da fração rutila e da absorção óptica, o que também foi associado a um aumento da concentração de defeitos eletrônicos. A análise dos filmes onde o fluxo de oxigênio foi sistematicamente interrompido durante a deposição mostrou que o aumento no número de interrupções não interferiu significativamente na morfologia colunar dos filmes, mas produziu um considerável aumento na fração rutila dos filmes, bem como um aumento na absorção óptica sub-gap. O aumento na absorção na região do visível e infravermelho próximo foi atribuído a um aumento na concentração de defeitos que, de acordo com cálculos baseados na teoria do funcional da densidade, estão relacionados a estados de energia provenientes de vacâncias de oxigênio. Os filmes de TiO2 dopados com diferentes concentrações de Mn pertencentes ao terceiro grupo tambémpt
dc.description.abstractThe search for a better understanding of the interrelation between the parameters involved in the process of film growth and the resulting structural, electronic and magnetic properties was the main motivation of this work. To the purpose, TiO2 films were grown by RF magnetron sputtering technique in different conditions. In a first set, TiO2 films were deposited with continuous O2 flow. In another set, systematic interruptions in the O2 flow were performed during the deposition. The last group of samples was deposited using a continuous O2 flow and Mn doping. A detailed analysis of the first group showed that these films exhibit columnar morphology with mainly anatase structure and optical gap of ~3.3eV, independent of the substrate temperature (450ºC and 600ºC) and the ratio used. THe decrease in O2 flux caused an increase in the sug gap absorption which associated with the increase in electronic defects of the material. Anneling in vacuum at 800ºC performed on pure TiO2 films showed an increase in the rutilo fraction, a red shift of the optical absorption edge, and an increase of the sub gap absorption associated with the increase of the electronic defects. The analysis of the films were the O2 flow was systematically interrupted during the deposition showed that the increase in the number of interruptions did not interfere significantly in the columnar morphology, but produced a significant increase in the fraction of rutile and brookite as well as an increase in sub-gap absorption. The increase in absorption in the visible and near infrared was attributable to an increase in the concentration of defects that, according to calculations based on the density functional theory, should be related to energy states provides by O vacancies. The Mn doped films also present a compact columnar morphology and a strong and systematic favoring of the rutile... (Complete abstract click electronic access below)en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.format.extent131 f. : il.
dc.identifier.aleph000706283
dc.identifier.capes33004056083P7
dc.identifier.citationPEREIRA, Andre Luis de Jesus. Otimização do processo de deposição de filmes TiO2:Mn usando RF magnetron sputtering. 2012. 131 f. Tese (doutorado) - Universidade Estadual Paulista, Faculdade de Ciências, 2012.
dc.identifier.filepereira_alj_dr_bauru.pdf
dc.identifier.lattes1134426200935790
dc.identifier.lattes1353862414532005
dc.identifier.orcid0000-0002-7734-4069
dc.identifier.urihttp://hdl.handle.net/11449/106646
dc.language.isoeng
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectDióxido de titâniopt
dc.subjectFilmes finospt
dc.subjectCrepitação (Fisica)pt
dc.subjectTitanium dioxidept
dc.subjectThin filmspt
dc.subjectSputtering (Physics)pt
dc.titleOtimização do processo de deposição de filmes TiO2:Mn usando RF magnetron sputteringen
dc.typeTese de doutorado
unesp.advisor.lattes1353862414532005[2]
unesp.advisor.orcid0000-0002-7734-4069[2]
unesp.author.lattes1134426200935790
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Ciências, Baurupt
unesp.graduateProgramCiência e Tecnologia de Materiais - FCpt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Carregando...
Imagem de Miniatura
Nome:
pereira_alj_dr_bauru.pdf
Tamanho:
5.04 MB
Formato:
Adobe Portable Document Format