Influência da presença e do tipo de retentor intrarradicular no comportamento em fadiga de incisivos centrais restaurados com coroas totais

Página do item simplificado
dc.contributor.advisorSaavedra, Guilherme de Siqueira Ferreira Anzaloni [UNESP]
dc.contributor.authorde Andrade, Guilherme Schmitt [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2019-01-23T13:10:15Z
dc.date.available2019-01-23T13:10:15Z
dc.date.issued2019-01-07
dc.description.abstractEste estudo avalia a influência da presença e tipo de pinos e núcleos na sobrevivência à fadiga de incisivos centrais restaurados com coroas totais. As coroas de 69 incisivos bovinos foram cortadas e as raízes tratadas endodonticamente. As raízes foram distribuídas aleatoriamente em três grupos (n = 23): núcleo de resina composta (NRC), núcleo de resina composta retido por pino de fibra de vidro (PFV) e núcleo metálico fundido (NMF). Todos receberam preparo de coroa total com férula de 2 mm, e então, uma coroa de cerâmica reforçada com leucita foi adesivamente cimentada. Três amostras de cada grupo foram testadas para determinação da carga máxima até a falha. As amostras restantes foram carregadas pelo teste acelerado de fadiga stepwise stress até a fratura ou suspensão após o término de 1,5 x 106 ciclos. A carga e o degrau em que cada espécime falhou foram analisadas pela estatística de Kaplan-Meier e Mantel-Cox (Log Rank test), seguidas por comparação múltipla aos pares, com nível de significância de 5%. O modo de falha foi analisado com estéreomicrocópio. Não houve diferença estatística entre os tratamentos quanto à carga (Mantel-Cox Log-Rank test for trend, X2=0,015, df=1, p=0,901), nem para o número de ciclos (Mantel-Cox Log-Rank test for trend, X2 =3,171, df=1, p=0,995). O modo de falha predominante foi a trinca da coroa. Fratura obliqua da raiz só foi observado nos grupos retidos por pinos. Nos incisivos tratados endodonticamente com férula de 2 mm, a presença e o tipo de pino e núcleo não influenciaram na sobrevida em fadiga. Fraturas não restauráveis ocorreram somente em dentes restaurados com pinos.pt
dc.description.abstractThis study evaluates the influence of presence and type of post-and-core systems on fatigue survival of non-vital central incisors restored with all-ceramic crowns. The crowns of 69 bovine incisors were cut and endodontically treated. The roots were randomly assigned into three groups (n=23): composite resin build-up (NRC), glass fiber post-retained-composite build-up (PFV) and cast post-and-core (NMF). All specimens received crown preparation with a 2 mm ferrule, and then a leucite-reinforced ceramic crown was adhesively cemented. Three samples from each group were tested for the determination of the maximum load to failure. The remaining samples were loaded by the accelerated fatigue stepwise stress test until fracture or suspension after the end of 1.5 x 106 cycles. The load and the step on which each specimen failed were analyzed by the Kaplan-Meier and Mantel-Cox (Log Rank test) statistics, followed by multiple paired comparisons, with a significance level of 5%. The failure mode was analyzed with stereomicroscope. There was no statistically significant difference between the treatments (Mantel-Cox Log-Rank test for trend, X2=0.015, df=1, p=0.901), nor for the number of cycles (Mantel-Cox Log-Rank test for trend, X2=3.171, df=1, p=0.995). The predominant failure mode was the crown crack. Oblique root fracture was observed only in groups retained by posts. The presence and type of post system did not influence the fatigue survival of the endodontically treated incisors with a 2 mm ferrule. Non-restorable fractures only occurred on teeth restored with posts.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.identifier.aleph000911934
dc.identifier.capes33004145070P8
dc.identifier.urihttp://hdl.handle.net/11449/180531
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subjectFadigapt
dc.subjectTécnica para retentor intrarradicularpt
dc.subjectDente tratado endodonticamentept
dc.subjectCoroas dentáriaspt
dc.subjectFatiguept
dc.subjectFatigueen
dc.subjectPost and core techniqueen
dc.subjectEndodontically treated teethen
dc.subjectCrownsen
dc.titleInfluência da presença e do tipo de retentor intrarradicular no comportamento em fadiga de incisivos centrais restaurados com coroas totaispt
dc.title.alternativeInfluence of the presence and type of post-and-core on the fatigue behavior of crowned central incisorsen
dc.typeDissertação de mestrado
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargoOnlinept
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesempenho de Materiais Reabilitadores Protéticospt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
andrade_gs_me_sjc.pdf
Tamanho:
2.12 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.04 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Dissertações - Odontologia Restauradora - ICT