Publicação: Precipitation reaction in alpha-Cu-Al-Ag alloys
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Rede Latino-Americana de Materiais
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The results indicated that the Ag-rich phase formation is an interface controlled process with a zero-order mechanism, due to the amount of unsolved Ag that makes the precipitation reaction rate independent of Ag concentration.
Descrição
Palavras-chave
Ag additions, Cu-based alloys, kinetics
Idioma
Inglês
Como citar
Matéria (Rio de Janeiro). Rede Latino-Americana de Materiais, v. 16, n. 3, p. 747-753, 2011.
Itens relacionados
Financiadores
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)