High-Pressure Assisted Sintering of Ti-20Si-10B and Ti-10Si-5B Powders
Carregando...
Arquivos
Fontes externas
Fontes externas
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Trans Tech Publications Ltd
Tipo
Trabalho apresentado em evento
Direito de acesso
Arquivos
Fontes externas
Fontes externas
Resumo
This work presents the structural characterization of Ti-10Si-5B and Ti-20Si-10B (at-%) alloys produced by high-pressure assisted sintering. Sintering was performed in air at 1100 and 1200 degrees C for 60 s using pressure levels of 5 GPa. Structural evaluation of sintered samples was conducted by means of scanning electron microscopy and energy dispersive spectrometry. Samples were successfully consolidated after sintering, which presented theoretical density values higher than 99%. The microstructures of the sintered Ti-10Si-5B and Ti-20Si-10B alloys revealed the presence of the Ti-SS, TiB, TiB2, Ti5Si3, Ti5Si4, TiSi, and TiSi2. phases. A small amount of Ti6Si2B was formed after high-pressure assisted sintering of the Ti-20Si-10B alloy (5GPa, 1100 degrees C for 60 s) indicating that equilibrium structures were not achieved during short sintering times. No oxygen and carbon contamination was detected in structures of Ti-Si-B alloys after high-pressure sintering at 1100 and 1200 degrees C without controlled atmosphere.
Descrição
Palavras-chave
titanium alloys, electron microscope, powder metallurgy, sintering
Idioma
Inglês
Citação
Advanced Powder Technology Viii, Pts 1 And 2. Durnten-zurich: Trans Tech Publications Ltd, v. 727-728, p. 462-+, 2012.