Publicação: Phase transformation in mechanically alloyed and hot-pressed Nb-4Si-8B and Nb-8Si-16B alloys
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Trabalho apresentado em evento
Direito de acesso
Resumo
The work reports on the phase transformation in mechanically alloyed and hot-pressed Nb-4Si-8B and Nb-8Si-16B (at-%) alloys. Elemental powder mixtures were processed in a planetary ball mill under argon atmosphere using 300 rpm, stainless steel balls (19 mm diameter) and vials (225 mL), and a ball-to-powder weight ratio of 10:1. After dry milling for 7h, wet milling with isopropyl alcohol for more 20 min was adopted to increase the recovering of previously coldwelded Nb-4Si-8B powders. To obtain the equilibrium structures the as-milled powders were hotpressed under vacuum at 1200oC for 1 h. The as-milled powders and hot-pressed samples were characterized by X-ray diffraction, scanning electron microscopy, and energy dispersive spectrometry. XRD results revealed the presence of metastable phases in as-milled Nb-Si-B powders. The hot pressing has produced dense Nb-Si-B samples, which were formed by the Nbss, Nb3B2and Fe2Nb phases beside of other unknown Si-rich phase.
Descrição
Palavras-chave
Contamination, High-energy ball milling, Hot pressing, Niobium alloys
Idioma
Inglês
Como citar
Materials Science Forum, v. 802, p. 14-19.