Analysis of the bioactive surface of Ti-35Nb-7Zr alloy after alkaline treatment and solution body fluid
Nenhuma Miniatura disponível
Data
2013-02-28
Autores
Schneider, S. G.
Escada, A. L A [UNESP]
Carvalho, E. T A
Alves-Claro, A. P R [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
The purpose of this work was to evaluate the Ti-35Nb-7Zr experimental alloy after surface treatment and soaking in solution body fluid (SBF) to form bonelike apatite. The Ti-35Nb-7Zr alloy was produced from commercially pure materials (Ti, Nb and Zr) by an arc melting furnace. All ingots were submitted to sequences of heat treatment (1100 °C/2 h and water quenching), cold working by swaging procedures and heat treatment (1100 °C/2 h and water quenching). Discs with 13 mm diameter and 3 mm in thickness were cut. The samples were immersed in NaOH aqueous solution with 5 M at 60 °C for 72 h, washed with distilled water and dried at 40 °C for 24 h. After the alkaline treatment, samples were heat treated in both conditions: at 450 and 600 °C for 1 h in an electrical furnace in air. Then, they were soaking in SBF for 24 h to form an apatite layer on the surface. The surfaces were investigated by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and contact angle measurements. The results indicate that calcium phosphate could form on surface of Ti-35Nb-7Zr experimental alloy. © Springer-Verlag Berlin Heidelberg 2013.
Descrição
Palavras-chave
Bioactivity, Surface treatment, Titanium alloys
Como citar
Advanced Structured Materials, v. 29, p. 143-152.