Desenvolvimento de pastilhas cerâmicas à bases de Si3N4 para aplicações tribológicas

Página do item simplificado
dc.contributor.advisorCrnkovic, Sérgio João [UNESP]
dc.contributor.advisorSilva, Olivério Moreira de Macedo [UNESP]
dc.contributor.authorSouza, José Vitor Cândido de [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:34:58Z
dc.date.available2014-06-11T19:34:58Z
dc.date.issued2005
dc.description.abstractNesse trabalho foram desenvolvidas três composições à base de Si3N4 com quantidades e tipos de aditivos diferentes, com objetivos de desenvolver cerâmicas densas de altas resistências, para posteriores testes como ferramentas de corte na usinagem de torneamento do ferro fundido cinzento, ferro fundido vermicular e a liga Ti-6Al-4V. As composições utilizaram aditivos Y2O3/Al2O3 (10%) e AlN/Y2O3 (15 e 20%), e foram sinterizadas pelo processo de sinterização normal. Em seguida foram caracterizadas quanto as propriedades físicas e mecânicas, apresentando bons resultados. Posteriormente a composição de melhores propriedades (SNYA20), foi transformada em inserto para usinagem de corte de acordo com a norma ISO 1832. Os testes de torneamento foram realizados no ferro fundido cinzento com variações de parâmentros, onde para Vc=300m/min, f=0,32mm/rot e ap=1,00mm, alcançou um comprimento de corte de 6533m, superior aos encontrados em literatura, com diminuição dos desgastes, para maiores Vc e ap. O torneamento da liga Ti-6Al-4V em alta velocidade (Vc=180m/min, f=0,10mm/rot e ap=0,50mm), alcançou comprimento de corte de Lc=466m, para um desgaste VBmax=2,20mm. No torneamento do ferro fundido vermicular, com variações de parâmetros, alcançou resultados superiores aos encontrados na literatura com ferramentas cerâmicas comercial, utilizando Vc=200mm/min, f=0,20mm/rot e ap= 0,50mm, obteve-se comprimento de corte Lc=1658m. Os resultados de usinagem obtidos nesse trabalho estão relacionados com as propriedades e fases obtidas. Entretanto alem dos resultados obtidos essas ferramentas apresentam custo em torno de 50% das comerciais e redução de 17- 20% de custo no processo, devido ao uso de fluido refrigerante e proteção ao meio ambiente.pt
dc.description.abstractIn this work three compositions to base Si3N4 with amounts and types of different additives had been developed, with objective to develop dense ceramics of high strength to possible test as cutting tools in turning of gray cast iron, compacted graphite iron and titanium alloy (Ti-6Al-4V). The compositions had used additives Y2O3/Al2O3 (10%) and AlN/Y2O3 (15 and 20%), and were sinterized by process normal sintering. After sintering the physical and mechanical properties had been characterized, showing interesting results. Posterior the composition the best properties (SNYA20), was transformed into cutting tools to machining in the stand norm ISO 1832. The turning tests had been carried in gray cast iron with different parameters, where to Vc=300m/min, f=0,32mm/rev and ap=1,00mm, obtained a cut length of 6533m, achieving value superior at found in literature, with important reduction to larger cutting speed and cut depth. The turning of the Ti-6Al-4V alloy in high cutting speed (Vc=180m/min, f=0,10mm/rev and ap=0,50mm), obtained cutting length of Lc=466m, to VBmax=2,20mm. In turning compacted graphite iron, with different parameters, obtained value superior at found in literature, when utilize cutting tools ceramics of commercial materials, using for this Vc=200mm/min, f=0,20mm/rev and ap = 0,50mm. These condition obtained cut length of Lc=1658m. The results achieved in this work have been associated with the important physical and mechanical proprieties and phase of cutting tools. However the results obtained with these cutting tools present lower cost (50%) when compared with commercial cutting tools of similar material e reduction of cost in around 17-20%, because the do not use coolant, beside of protection at environment.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipUniversidade Estadual Paulista (UNESP)
dc.format.extent134 f. : il.
dc.identifier.aleph000391315
dc.identifier.capes33004080027P6
dc.identifier.citationSOUZA, José Vitor Cândido de. Desenvolvimento de pastilhas cerâmicas à bases de Si3N4 para aplicações tribológicas. 2005. 134 f. Tese (doutorado) - Universidade Estadual Paulista, Faculdade de Engenharia de Guaratinguetá, 2005.
dc.identifier.filesouza_jvc_dr_guara.pdf
dc.identifier.urihttp://hdl.handle.net/11449/105366
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectMateriais compostospt
dc.subjectUsinagempt
dc.subjectFerro fundido cinzentopt
dc.subjectFerro fundido vermicularpt
dc.subjectFluido de cortept
dc.subjectTribologiapt
dc.subjectGray cast ironen
dc.subjectCompacted graphite ironen
dc.subjectCoolanten
dc.subjectTribologicalen
dc.titleDesenvolvimento de pastilhas cerâmicas à bases de Si3N4 para aplicações tribológicaspt
dc.typeTese de doutorado
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Engenharia, Guaratinguetápt
unesp.graduateProgramEngenharia Mecânica - FEGpt
unesp.knowledgeAreaProjetos e materiaispt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
souza_jvc_dr_guara.pdf
Tamanho:
3.28 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Teses - Engenharia Mecânica - FEG