Efeito de diferentes tratamentos de superfície na resistência ao cisalhamento entre uma resina nanohíbrida para impressão 3D e cimento resinoso

Página do item simplificado
dc.contributor.advisorBottino, Marco Antonio [Unesp]
dc.contributor.advisorRibeiro, Nathália de Carvalho Ramos
dc.contributor.authorRodriguez, Rita Maria Morejon
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2023-06-23T13:46:05Z
dc.date.available2023-06-23T13:46:05Z
dc.date.issued2023-03-22
dc.description.abstractO objetivo deste trabalho foi avaliar a resistência de união entre uma resina nanohíbrida para impressão 3D com cimento resinoso após diferentes tratamentos de superfície e envelhecimento. Foram fabricados 120 blocos da resina nanohíbrida (Nanolab 3D, Wilcos do Brasil) em tamanhos de 10 x 8 x 2 mm, desenhados no software Rhinoceros 7 e depois impressos (W3D PRINT, Wilcos do Brasil) por método digital de processamento de luz (LCD). Foram produzidos também blocos de mesmo tamanho obtidos a partir de blocos de CAD/CAM de uma resina híbrida (Hybrid, Blue Dent), como grupo controle. Cinco tratamentos de superfície foram realizados nos blocos de resina: nenhum tratamento, condicionamento ácido com ácido fluorídrico, jateamento com Al3O2 , imersão em monômero de metilmetacrilato (primer) e um grupo somando o jateamento com imersão em primer. Foram construídos cilindros (< 1 mm2 ) de cimento resinoso convencional dual sobre as superfícies tratadas com auxílio de matriz de silicone. A resistência de união foi medida usando uma máquina de ensaio universal e um teste de microcisalhamento com fio. Metade das amostras de cada grupo foram testadas sete dias após a cimentação, já a outra metade foi termociclada por 12.000 ciclos térmicos (5-55 oC, 30 segundos cada) e ensaiadas a seguir. Os modos de falha foram analisados por um estereomicroscópio e imagens representativas foram realizadas com o auxílio do microscópio eletrônico de varredura. Após a análise inferencial com ANOVA 3-fatores foi possível observar que houve diferença estatisticamente significante tanto para os fatores material, tratamento de superfície e envelhecimento isoladamente, como para as interações entre eles. A resina híbrida de impressão mostrou maior resistência de união quando comparada com os blocos CAD/CAM. A ciclagem térmica aumentou a resistência de união das resinas impressas e diminuiu a mesma nos blocos de CAD/CAM. É possível concluir que a aplicação de silano é o melhor tratamento de superfície para as resinas de impressão 3D já que proporcionou bons valores de resistência de união e confiabilidade da interface adesiva. A resistência adesiva a longo prazo da resina híbrida de impressão 3D (Nanolab) é influenciada positivamente pelo envelhecimento.pt
dc.description.abstractThe objective of this work was to evaluate the bond strength between a nanohybrid resin for 3D printing with resin cement after different surface treatments and aging. 120 blocks of nanohybrid resin (Nanolab 3D, Wilcos do Brasil) were manufactured in sizes of 10 x 8 x 2 mm, designed in the Rhinoceros 7 software and then printed (W3D PRINT, Wilcos do Brasil) by digital light processing method (LCD ). Blocks of the same size obtained from CAD/CAM blocks of a hybrid resin (Hybrid, Blue Dent) were also produced as a control group. Five surface treatments were performed on the resin blocks: no treatment, acid etching with hydrofluoric acid, sandblasting with Al3O2, immersion in methylmethacrylate monomer (primer) and one group adding the sandblasting with immersion in primer. Cylinders (< 1 mm2) of conventional dual resin cement were built on the surfaces treated with the aid of a silicone matrix. Bond strength was measured using a universal testing machine and a wire microshear test. Half of the samples from each group were tested seven days after cementation, while the other half was thermocycled through 12,000 thermal cycles (5-55 ºC, 30 seconds each) and then tested. Failure modes were analyzed using a stereomicroscope and representative images were taken using a scanning electron microscope. After the inferential analysis with 3-way ANOVA, it was possible to observe that there was a statistically significant difference both for the material, surface treatment and aging factors alone, as well as for the interactions between them. The hybrid impression resin showed higher bond strength when compared to the CAD/CAM blocks. Thermal cycling increased the bond strength of printed resins and decreased it in CAD/CAM blocks. It is possible to conclude that silane application is the best surface treatment for 3D printing resins as it provided good bond strength values and reliability of the adhesive interface. The long-term adhesive strength of the 3D printing hybrid resin (Nanolab) is positively influenced by aging.en
dc.identifier.capes330041415070P8
dc.identifier.urihttp://hdl.handle.net/11449/244175
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subject3D Printpt
dc.subjectresinaspt
dc.subjectadesividadept
dc.subjectciência dos materiaispt
dc.subject3D Printingen
dc.subjectresinsen
dc.subjectadhesivenessen
dc.subjectmaterials scienceen
dc.titleEfeito de diferentes tratamentos de superfície na resistência ao cisalhamento entre uma resina nanohíbrida para impressão 3D e cimento resinosopt
dc.title.alternativeEffect of different surface treatments on the shear strength between a nanohybrid resin for 3D printing and resin cementen
dc.typeDissertação de mestrado
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargoOnlinept
unesp.examinationboard.typeBanca públicapt
unesp.graduateProgramCiências Aplicadas à Saúde Bucal - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesempenho de materiais reabilitadores protéticospt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
rodriguez_rmm_me_sjc.pdf
Tamanho:
13.87 MB
Formato:
Adobe Portable Document Format
Descrição:
Artículo principal
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.04 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Instituto de Ciência e Tecnologia, São José dos Campos