Novo formato de pilar protético em zircônia estabilizada por Itría (Y-Tzp) para implantodontia desenvolvido pela técnica de slip casting

Página do item simplificado
dc.contributor.advisorTango, Rubens Nisie [UNESP]
dc.contributor.authorSilva, Lucas Hian da [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:28:57Z
dc.date.available2014-06-11T19:28:57Z
dc.date.issued2011-07-08
dc.description.abstractO objetivo deste estudo foi desenvolver um novo formato de pilar protético estético em zircônia (3Y-TZP) visando suprimir a utilização do parafuso trespassante utilizado no formato convencional de pilares protéticos em zircônia. Inicialmente foi feita a caracterização do material utilizado na técnica de colagem de barbotina (slip casting) através da confecção de uma barra que teve suas propriedades mecânicas, módulo de elasticidade (E) e coeficiente de Poisson (), grau de contração e dimensão de suas partículas após sinterização avaliados pelos métodos de frequências naturais de vibração e microscopia eletrônica de varredura (MEV), respectivamente. Previamente à confecção do pilar protótipo, este teve seu comportamento mecânico avaliado e comparado a um pilar de 3YTZP convencional com parafuso trespassante pela análise por elementos finitos (FEA) durante sua instalação em implante e recebendo carga oblíqua simulando força de mastigação (210,5 N). O protótipo foi confeccionado pela técnica de colagem de barbotina em um molde de gesso obtido a partir de uma duplicata ampliada em cera. A densidade final foi avaliada pelo método de Archimedes em água. Obteve-se o módulo de elasticidade de 187,97 ± 4,84 GPa e coeficiente de Poisson de 0,19 ± 0,04 para o material. O grau de contração de sinterização foi de 58 vol% e o tamanho do grão foi de 0,705 ± 0,424 μm. Na análise por FEA verificou-se concentrações de tensões na região inicial da rosca para ambos os pilares, e durante o carregamento foram observadas tensões de tração no lado em que incidiu a carga, com presença de tensões de compressão no lado oposto. Ainda, observou-se durante o carregamento do pilar protético convencional concentração de tensão na região do pescoço do parafuso trespassante. A densidade final obtida para o pilar protótipo em 3Y-TZP foi de 95,68% em...pt
dc.description.abstractThe purpose of this study was to develop a new esthetic zirconia (3YYTZP) implant abutment shape to suppress the use of the fixing screw commonly used by the conventional zirconia abutments. A material characterization, Young’s modulus (E), Poisson’s rate (), shrinkage and particles dimensions after sintering was performed for a bar shape specimen obtained by slip casting evaluated by the natural torsional and flexural vibration frequencies and scanning electron microscope (SEM), respectively. Previously to the prototype abutment confection, its mechanical behavior was evaluated and compared to a conventional zirconia abutment with a fixing screw by finite element analisys (FEA) simulating the abutment installation and oblique loading (210.5 N). The prototype was confectioned by the slip casting technique using a gypsum mould obtained from a wax expanded replica. The abutment had its density measured by Archimedes’ method. Through the natural vibration frequencies a Young’s modulus of 187.97 ± 4.84 GPa and a Poisson’s rate of 0.19 ± 0.04 were obtained for the material. The shrinkage was 58 vol% and the grain size was 0,705 ± 0,424 μm . The FEA showed stress concentration at the first thread pitch for both abutments, and tensile stress concentration were observed at the side that received the oblique load with compressive stress at the opposite side. Whereas, for the conventional abutment model a stress concentration was observed at the screw’s stem. The final density for the zirconia prototype abutment was 95.68% from the theoretical density (6.12 g.cm-3). The zirconia abutment obtained by slip casting presented satisfactory physical properties. The suppressing of the fixing screw could provide better performance to the abutment due to the lack of stress concentration in the screw when an oblique load is applied, when evaluated by FEAen
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent127 f. : il., tabs.
dc.identifier.aleph000651063
dc.identifier.capes33004145070P8
dc.identifier.citationSILVA, Lucas Hian da. Novo formato de pilar protético em zircônia estabilizada por Itría (Y-Tzp) para implantodontia desenvolvido pela técnica de slip casting. 2011. 127 f. Dissertação (mestrado) – Universidade Estadual Paulista, Faculdade de Odontologia de São José dos Campos, 2011.
dc.identifier.filesilva_lh_me_sjc.pdf
dc.identifier.lattes9138716680440603
dc.identifier.orcid0000-0003-0946-1826
dc.identifier.urihttp://hdl.handle.net/11449/97343
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectOxido de zirconiopt
dc.subjectMicroscopia eletronica de varredurapt
dc.subjectPrótese dentáriapt
dc.subjectColagem de barbotinapt
dc.subjectPilares de implantes dentáriosen
dc.subjectSlip castingen
dc.subjectScanning electron microscopeen
dc.subjectDental prosthesisen
dc.subjectDental implantsen
dc.titleNovo formato de pilar protético em zircônia estabilizada por Itría (Y-Tzp) para implantodontia desenvolvido pela técnica de slip castingpt
dc.typeDissertação de mestrado
unesp.advisor.lattes9138716680440603
unesp.advisor.orcid0000-0003-0946-1826
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaAvaliação clínica e laboratorial de materiais e técnicas em prótesept

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
silva_lh_me_sjc.pdf
Tamanho:
2.39 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Dissertações - Odontologia Restauradora - ICT