Resistência adesiva de bráquetes ortodônticos colados com sistemas adesivos convencionais e auto-condicionantes ao esmalte bovino após ciclos térmicos e termomecânicos

Página do item simplificado
dc.contributor.advisorNicoló, Rebeca Di [UNESP]
dc.contributor.authorTorres, Luciana Marcondes Sarmento [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:24:07Z
dc.date.available2014-06-11T19:24:07Z
dc.date.issued2011-06-29
dc.description.abstractEste estudo in vitro teve como objetivo avaliar a influência das ciclagens térmica e termomecânica na resistência adesiva de bráquetes colados em esmalte bovino com primers convencionais e auto-condicionates. Noventa incisivos bovinos foram aleatoriamente divididos em 2 grupos (G), de acordo com o primer utilizado: XT (n=45) – bráquetes colados com primer convencional (Transbond XT/3M, Unitek); SEP (n=45) – bráquetes colados com primer auto-condicionante (Transbond Plus SEP/3M, Unitek). Após a colagem dos bráquetes, cada grupo foi subdividido em 3 subgrupos (n=15): SC (sem ciclagem) – as amostras não receberam nenhum tipo ciclagem; CT (ciclagem térmica) – as amostras receberam apenas ciclagem térmica (500 ciclos de 50C a 550C); CTM (ciclagem termomecânica) – as amostras receberam ciclagem termomecânica (100.000 ciclos de 50C a 550C). A seguir, foi realizado o teste de cisalhamento em uma máquina de ensaios universal (EMIC) a uma velocidade de 1mm/min com célula de carga de 100kg. Após o descolamento dos bráquetes, amostras de cada grupo foram submetidas à avaliação microscópica em microscópio eletrônico de varredura, a fim de analisar a superfície do esmalte e quantificar o Índice de Adesivo Remanescente (IAR) sobre a superfície. Os resultados mostraram que o grupo SEP apresentou maior resistência adesiva (14,70±4,85 MPa) quando comparado com o grupo XT (11,27±4,48 MPa). Para os grupos XT, a resistência adesiva manteve-se semelhante independente do tipo de ciclagem (SC, 11,44 MPa; CT, 11,20 MPa; CTM,11,19 MPa), enquanto que para os grupos SEP o subgrupo CTM foi o que apresentou maiores valores de resistência adesiva (16,84 MPa), seguido do CT (14,99 MPa) e SC (12,26 MPa). O teste ANOVA - 2 fatores revelou que o efeito interação não é estatisticamente significante; indicando, assim, que o efeito do tipo de ciclagem para o grupo XT é o mesmo...pt
dc.description.abstractThe aim of this in vitro study was to evaluate the influence of thermal and thermomechanical cycling on shearbond strength of orthodontic brackets bonded with conventional and self-etching primers. 90 bovine incisors were randomly divided into 2 groups (G) according to the primer: XT (n=45) – brackets bonded with conventional primer (Transbond XT/3M, Unitek); SEP (n=45) – brackets bonded with self-etching primer (Transbond Plus SEP/3M, Unitek). After bonding, each group were divided into 3 subgroups (n=15): NC (no cycling) – the specimens did not receive any kind of cycling; TC (thermal cycling) – the specimens received only thermal cycling (500 cycles); TMC (thermomechanical cycling) – the specimens received thermomechanical cycling (100.000 cycles). Next, the shearbond strength test was performed in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. After debonding, specimens of each group were submitted to microscopic evaluation in order to analyze the enamel surface, the adhesive penetration and quantify the Adhesive Remaining Index (ARI). The results showed that the SEP group presented higher bond strength (14,70±4,85 MPa) compared with XT (11,27±4,48 MPa). For XT, the bond strength remained similar despite cycling (NC, 11,44 MPa; TC, 11,20 MPa; TMC,11,19 MPa), meanwhile for SEP, the subgroup TMC showed higher values of bond strength (16,84 MPa), followed by TC (14,99 MPa) e NC (12,26 MPa). 2-way ANOVA test indicated that the interaction effect is not statistically different, so the kind of cycling effect for XT is equal for SEP. But the primer effect (XT vs SEP) is statiscally significant. According to the ARI , the group that presented the highest remaining adhesive on the enamel surface was SEP/TMC (ARI=3). The results showed that self-etching primers can be safely used in orthodontic practice because presents adequate values of bond strength ... (Complete abstract click electronic access below)en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent107 f. : il. color., gráfs., tabs.
dc.identifier.aleph000651326
dc.identifier.capes33004145070P8
dc.identifier.citationTORRES, Luciana Marcondes Sarmento. Resistência adesiva de bráquetes ortodônticos colados com sistemas adesivos convencionais e auto-condicionantes ao esmalte bovino após ciclos térmicos e termomecânicos. 2011. 107 f. Dissertação (mestrado) – Universidade Estadual Paulista, Faculdade de Odontologia de São José dos Campos, 2011.
dc.identifier.filetorres_lms_me_sjc.pdf
dc.identifier.lattes4153738182937249
dc.identifier.orcid0000-0001-9132-0429
dc.identifier.urihttp://hdl.handle.net/11449/89592
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectResistência ao cisalhamentopt
dc.subjectOrtodontiapt
dc.subjectIncisivos (Dentes)pt
dc.subjectOrthodonticsen
dc.subjectShear strengthen
dc.subjectIncisorsen
dc.titleResistência adesiva de bráquetes ortodônticos colados com sistemas adesivos convencionais e auto-condicionantes ao esmalte bovino após ciclos térmicos e termomecânicospt
dc.typeDissertação de mestrado
unesp.advisor.lattes4153738182937249
unesp.advisor.orcid0000-0001-9132-0429
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaDentísticapt
unesp.researchAreaAvaliação clínica e laboratorial de materiais e novas técnicas em dentísticapt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
torres_lms_me_sjc.pdf
Tamanho:
1.23 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Dissertações - Odontologia Restauradora - ICT