Publicação: Dy3+/Tb3+-codoped tunable warm light-emitting fluorogermanate glass phosphor
Carregando...
Arquivos
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
Polychromatic tunable visible light emission in the region of the low correlated color temperature range using Dy3+/Tb3+ codoped PbGeO3:PbF2:CdF2 glass phosphor under UV-blue LED light excitation is presented. The glass phosphor was synthesized and the light emission feature was examined under UV-blue (353, 375, 385, and 405 nm) excitation. Emission around 484, 573, 663, and 754 nm due to dysprosium, and 488, 545, 585, 620, and 690 nm owing to terbium ions, was observed and analyzed as a function of the dysprosium and terbium contents and excitation wavelength. The excitation spectrum was examined and showed resonance peaks around 385 nm for the 573-nm emission of Dy3+, and 375 nm for the 545 nm of Tb3+. Energy-transfer process from Dy3+(F49/2) to Tb3+(D54) was also observed. Results indicated that the polychromatic visible light emitter herein reported produced light possessing tunable color tone via excitation wavelength and ions' mass ratio. The tint of the tunable overall emission resided in the warm region of the white-light boundary of the CIE-1931 chromaticity diagram.
Descrição
Palavras-chave
Phosphor, polychromatic, rare-earth, solid-state-lightining, warm-light, white-light emitting diode
Idioma
Inglês
Como citar
Optical Engineering, v. 55, n. 11, 2016.