Publicação: Influence of the indium concentration on microstructural and electrical properties of proton conducting NiO-BaCe0.9-xIn xY0.1O3-δ cermet anodes for IT-SOFC application
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Optimization of the major properties of anodes based on proton conductors, such as microstructure, conductivity and chemical stability, is yet to be achieved. In this study we investigated the influence of indium on the chemical stability, microstructural and electrical characteristics of proton conducting NiO-BaCe0.9-xInxY0.1O 3-δ (NiO-BCIYx) anodes. Four compositions of cermet anode substrates NiO-BCIYx were prepared using the method of evaporation and decomposition of solutions and suspensions (EDSS). Sintered anode substrates were reduced and their microstructural and electrical properties were examined before and after reduction as a function of the amount of indium. Anode substrates tested on chemical stability in the CO2 atmosphere showed high stability compared to anode substrates based on commonly used doped barium cerates. Microstructural properties of the anode pellets before and after testing in CO2 were investigated using X-ray diffraction analysis. Impedance spectroscopy measurements were used for evaluation of electrical properties of the anode pellets and the conductivity values of reduced anodes of more than 14 S cm-1 at 600 °C confirmed percolations through Ni particles. Under fuel cell operating conditions, the cell with a Ni-BCIY20 anode achieved the highest performance, demonstrating a peak power density 223 mW/cm2 at 700 °C confirming the functionality of Ni-BCIY anodes.© 2013 Elsevier B.V. All rights reserved.
Descrição
Palavras-chave
Anode, Cermet, Fuel cells, Protonic conductor, Doped barium cerate, Electrical characteristic, Impedance spectroscopy measurements, Indium concentration, Micro-structural properties, Operating condition, Peak power densities, Protonic conductors, Anodes, Carbon dioxide, Cermets, Chemical stability, Indium, Nickel, Pelletizing, Protons, Sintering, Solvents, Substrates, X ray diffraction analysis, Electric properties
Idioma
Inglês
Como citar
Journal of Alloys and Compounds, v. 563, p. 254-260.