Publicação: Efeito do envelhecimento hidrotérmico e mecânico na performance à fadiga de zircônias de alta translucidez
dc.contributor.advisor | Melo, Renata Marques de | |
dc.contributor.author | Prado, Pedro Henrique Condé Oliveira | |
dc.contributor.institution | Universidade Estadual Paulista (Unesp) | |
dc.date.accessioned | 2021-08-05T20:55:11Z | |
dc.date.available | 2021-08-05T20:55:11Z | |
dc.date.issued | 2021-07-07 | |
dc.description.abstract | O objetivo deste trabalho foi avaliar a resistência à fadiga e ciclos até a falha de 3 zircônias odontológicas após envelhecimento hidrotérmico isolado e um novo protocolo alternado. Discos de zircônia “Y”Z T (VITA), INCORIS “T”ZI (Dentsply Sirona) e “K”ATANA UTML (Noritake Kuraray) (N=135) – 1ª, 2ª e 3ª gerações, respectivamente –, foram divididos em 9 grupos (n=15), com 3 tratamentos para cada zircônia: CF – Controle, somente com fadiga mecânica; EF – Envelhecido em reator hidrotérmico a 134 ºC por 20 h + Fadiga; EFA: 4 passos de envelhecimentos de 5h alternados com fadiga. O teste de fadiga em flexão biaxial foi realizado com configuração de pistão sob 3 esferas, utilizando o método step-stress (carga inicial: 100 Mpa, step: 50 MPa/10.000 ciclos, frequência: 20 Hz). Os dados foram analisados através de teste Kaplan-Meir e Mantel-Cox com α=0,05, além da análise de Weibull. Discos fraturados foram analisados em estereomicroscópio, Microscopia Eletrônica de Varredura (MEV) e Difratômetro de Raios-X (DRX). O envelhecimento isolado com fadiga aumentou a resistência do grupo TEF (810 ± 76 MPa), enquanto diminuiu a do YEF (516 ± 38 MPa), o protocolo alternado aumentou a resistência apenas para a YZ T (730 ± 59 MPa). A KATANA UMTL não apresentou diferenças para ambos os tratamentos. Igualmente, foi a única a não sofrer transformação de fase T-M. O grupo TEF apresentou maior taxa sobrevivência à fadiga (147,000.00 ciclos). A origem de fratura para todos os espécimes deu-se no lado de tração em defeitos pré-existentes. Zircônias de 2ª geração possuem melhor comportamento mecânico e longevidade pós-envelhecimento e fadiga. Embora seja menos resistente, a KATANA UTML não sofreu degradação. | pt |
dc.description.abstract | This study aimed to evaluate the fatigue strength and cycles for failure of 3 dental zirconias after isolated and a novel hydrothermal and mechanical fatigue cycling aging protocol. “Y”Z T (VITA), INCORIS “T”ZI (Dentsply Sirona) and “K”ATANA UTML (Noritake Kuraray) zirconia discs (N=135), were divided into 9 groups (n=15), according to 3 proposed treatments for each zirconia: CF (control – only mechanical fatigue cycling); AF (aging in hydrothermal reactor at 134°C for 20 h + mechanical fatigue cycling ); AFA (Alternating protocol: 4 steps of 5 h of hydrothermal aging intercalated with mechanical fatigue cycling). Mechanical fatigue aging was performed according to the step stress approach through biaxial flexural setup (piston-on-3-balls, initial strength: 100 MPa, step: 50 MPa/ci000, frequency: 20 Hz) until failure. Data were analyzed using KaplanMeier and Mantel-Cox test (α=0.05), in addition to Weibull analysis. Fractured discs were analyzed in stereomicroscope, Scanning Electron Microscopy and XRay Diffraction. Continuous hydrothermal and mechanical fatigue cycling decreased the fatigue strength of YAF group (516 ± 38 MPa), while the alternating protocol increased it (730 ± 59 MPa). KATANA UTML showed no differences for both treatments and did not undergo T-M phase transformation. The TAF group showed the highest fatigue strength (810 ± 76 MPa) and cycles for failure (147,000.00 cycles). The fracture origin for all specimens was on the tensile side in pre-existing defects. INCORIS TZI zirconia have higher fatigue strength after hydrothermal and mechanical fatigue aging. Although less resistant, KATANA UTML did not suffer chemical degradation. | en |
dc.description.sponsorship | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) | |
dc.description.sponsorshipId | 88882.434258/2019-01 | |
dc.identifier.capes | 33004145070P8 | |
dc.identifier.uri | http://hdl.handle.net/11449/213893 | |
dc.language.iso | por | |
dc.publisher | Universidade Estadual Paulista (Unesp) | |
dc.rights.accessRights | Acesso aberto | |
dc.subject | Degradação | pt |
dc.subject | Cerâmicas odontológicas | pt |
dc.subject | Zircônia | pt |
dc.subject | Y-TZP | pt |
dc.subject | Fadiga | pt |
dc.subject | Degradation | en |
dc.subject | Dental ceramics | en |
dc.subject | Zirconia | en |
dc.subject | Y-TZP | en |
dc.subject | Fatigue | en |
dc.title | Efeito do envelhecimento hidrotérmico e mecânico na performance à fadiga de zircônias de alta translucidez | pt |
dc.title.alternative | Effect of hydrothermal and mechanical aging on the fatigue performance of high-translucency zirconias | en |
dc.type | Tese de doutorado | |
dspace.entity.type | Publication | |
unesp.campus | Universidade Estadual Paulista (UNESP), Instituto de Ciência e Tecnologia, São José dos Campos | pt |
unesp.embargo | Online | pt |
unesp.examinationboard.type | Banca pública | pt |
unesp.graduateProgram | Odontologia Restauradora - ICT | pt |
unesp.knowledgeArea | Prótese dentária | pt |
unesp.researchArea | Desempenho de materiais reabilitadores protéticos | pt |
Arquivos
Pacote Original
1 - 1 de 1
Carregando...
- Nome:
- prado_phc_dr_sjc.pdf
- Tamanho:
- 2.1 MB
- Formato:
- Adobe Portable Document Format
- Descrição:
Licença do Pacote
1 - 1 de 1
Carregando...
- Nome:
- license.txt
- Tamanho:
- 3.01 KB
- Formato:
- Item-specific license agreed upon to submission
- Descrição: