Strength of a feldspar ceramic according to the thickness and polymerization mode of the resin cement coating
Loading...
External sources
External sources
Date
Advisor
Coadvisor
Graduate program
Undergraduate course
Journal Title
Journal ISSN
Volume Title
Publisher
Japanese Soc Dental Materials Devices
Japanese Society for Dental Materials and Devices
Japanese Society for Dental Materials and Devices
Type
Article
Access right
Acesso aberto
External sources
External sources
Abstract
The aim of this study was to evaluate, in vitro, the biaxial flexural strength (ISO 6872) of a feldspathic ceramic (VM7, Vita Zahnfabrik) coated with a resin cement with different thicknesses and polymerization mode. Control groups consisted in VM7 with and without acid etching with 10% hydrofluoric acid for 1 min. Experimental groups comprised VM7 etched, silanated and coated with Variolink (Ivoclar Vivadent) cement, that was polymerized through the porcelain in light-cure and dual-cure modes, with thickness <= 150 mu m or > 150 mu m. The specimens (n=15) were subjected to the biaxial flexural strength essay and analyzed fractographically. Parametric (Dunnet, Anova 2-way, Tukey) and non-parametric tests (Weibull) were used to evaluate results. Ceramic disks coated with resin cements of either activation modes and thicknesses exhibited higher flexural strength while the Weibull moduli did not present significant differences for a confidence interval of 95%.
Description
Keywords
Language
English
Citation
Dental Materials Journal. Tokyo: Japanese Soc Dental Materials Devices, v. 30, n. 3, p. 323-329, 2011.