Avaliação da resistência à flexão de resinas para prótese do tipo protocolo
Loading...
Date
Authors
Advisor
Pinelli, Lígia Antunes Pereira 
Coadvisor
Graduate program
Undergraduate course
Araraquara - FOAR - Odontologia
Journal Title
Journal ISSN
Volume Title
Publisher
Universidade Estadual Paulista (Unesp)
Type
Undergraduate thesis
Access right
Acesso restrito
Abstract
Abstract (portuguese)
Uma elevada resistência à flexão é uma característica importante para resinas de base de prótese do tipo protocolo, uma vez que essas estruturas suportam cargas mastigatórias elevadas, o que exige alta resistência mecânica para evitar fraturas e garantir a durabilidade da prótese. O objetivo deste estudo foi avaliar a resistência à flexão (RF) de resinas utilizadas na confecção de próteses totais. Para tanto, foram confeccionados corpos de prova (62 × 8 × 3,3 ± 0,3 mm, n = 13 por grupo) de duas resinas acrílicas: impressa PriZma Bio Denture (Makertech Labs, grupo G1) e Ivo Base High Impact (Ivoclar, grupo G2, controle). As amostras impressas foram desenhadas em software Meshmixer e enviadas para impressão na impressora Flashforge, com espessura de camada de 48 µm e ângulo de impressão de 43°. Os espécimes de resina impressa foram incluídos em gesso tipo III, com muralha de silicone e mufla preenchida com gesso; a cera dos sprues foi eliminada em água fervente, seguido de isolamento com o separating fluid da Ivoclar. A resina High Impact foi injetada e polimerizada no sistema Ivobase (63 min). A mufla foi resfriada em água a 20 °C por 13 min e o acabamento inicial foi realizado com discos de aço e lixa 320. Após a confecção das barras, os espécimes de todos os grupos foram polidos manualmente com lixas de carbeto de silício de granulações 800 e 1200 e submetidos ao ensaio de flexão em três pontos em máquina universal de ensaios (EMIC DL2000, velocidade de 0,5 mm/min). Foi aplicado o teste estatístico de Mann-Whitney com nível de significância de 5%. Os valores médios e das medianas da RF (em MPa) foram: G1 = 89,3 ± 1,62 MPa; mediana = 90,1 MPa e G2 = 73,2 ± 5,0 MPa; mediana = 73,2 MPa, com diferença estatisticamente significativa entre os grupos. Conclui-se que a resina acrílica impressa apresentou maior resistência à flexão do que a resina acrílica injetada.
Abstract (english)
A high flexural strength is an essential characteristic for denture base resins used in protocol-type prostheses, as these structures must withstand high masticatory loads,
requiring high mechanical strength to prevent fractures and ensure the prosthesis's longevity. This study aimed to evaluate the flexural strength (FS) of resins used in the
fabrication of complete dentures. For this purpose, specimens (64 × 10 × 3.3 ± 0.03 mm, n = 15 per group) were prepared from two acrylic resins: printed PriZma Bio
Denture (Makertech Labs, group G1) and Ivo Base High Impact (Ivoclar, group G2, control). The printed samples were designed using Meshmixer software and printed
on a Flashforge printer with a layer thickness of 50 µm and a printing angle of 45°. The printed resin specimens were embedded in Type III gypsum with a silicone wall, and
the flask was filled with gypsum. The wax sprues were then eliminated by boiling water, followed by the application of Ivoclar separating fluid. The High-Impact resin was
injected and polymerized using the Ivobase system (65 minutes). The flask was cooled in water at 22 °C for 15 min, and initial finishing was performed with steel discs and
320-grit sandpaper. After bar fabrication, specimens from all groups were manually polished with silicon carbide sandpapers of 800 and 1200 grit and subjected to a threepoint bending test using a universal testing machine (EMIC DL2000, with a crosshead speed of 0.5 mm/min). The Mann-Whitney statistical test was applied with a significance level of 5%. The average and median FS values (in MPa) were as follows: G1 = 91.3 ± 6.64 MPa; median = 92.6 MPa, and G2 = 75.2 ± 5.00 MPa; median = 75.2 MPa, showing a statistically significant difference between the groups. It was concluded that the printed acrylic resin presented higher flexural strength than the injected acrylic resin.
Description
Keywords
Resinas acrílicas, Polimetil metacrilato, Resistência à flexão, Impressão tridimensiona, Acrylic resins, Polymethyl methacrylate, Flexural strength, Printing, three-dimensional
Language
Portuguese
Citation
Arellaro GA. Avaliação da resistência à flexão de resinas para prótese do tipo protocolo [Trabalho de Conclusão de Curso – Graduação em Odontologia]. Araraquara: Faculdade de Odontologia da UNESP; 2025.