Publicação: Structural characterization and ferroelectric properties of strontium barium niobate (Sr xBa1-xNb2O6) thin films
Carregando...
Data
Autores
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
ABM, ABC, ABPol
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
Strontium barium niobate (SBN) thin films of good quality were deposited on Pt/Ti/SiO2/Si substrate using a polymeric resin containing metallic ions. Films were crystallized at different temperatures and for different duration of time. The structure of these films was studied using X-ray diffraction. The coexistence of SrNb2O6 (SN) and SBN was observed in films crystallized at 700 °C. The amount of SN decreases when the crystallization time increases. Ferroelectric properties were determined for films crystallized at 700 °C for 1 and 5 h. For SBN film crystallized at 700 °C for 1 h, the remanent polarization (Pr) and the coercive field (Ec) were 2.6 muC/cm² and 71.9 kV/cm, respectively. For the film crystallized at 700 °C for 5 h these parameters were Pr = 1.1 muC/cm² and Ec = 50.5 kV/cm.
Descrição
Palavras-chave
thin films, SBN, tungsten bronze structure
Idioma
Inglês
Como citar
Materials Research. São Carlos, SP, Brazil: ABM, ABC, ABPol, v. 4, n. 2, p. 113-116, 2001.