Publicação: Tribocorrosion behaviour of hot pressed CoCrMo−Al2O3 composites for biomedical applications
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Alumina/alumina wear couple can lower the wear rates and thus metallic ion releasing on load bearing metallic implant materials. However, the low fracture toughness of ceramics is still a major concern. Therefore, the present study aims to process and to triboelectrochemically characterise the 5 and 10 vol.-%Al2O3 reinforced CoCrMo matrix composites. Corrosion and tribocorrosion behaviour of the composites were investigated in 8 g L−1 NaCl solution at body temperature. Corroded and worn surfaces were investigated by a field emission gun scanning electron microscope equipped with energy dispersive X-ray spectroscopy. After tribocorrosion experiments, wear rates were calculated using a profilometer. Results suggest that Al2O3 particle addition decreased the tendency of CoCrMo alloy to corrosion under both static and tribocorrosion conditions. However, no significant influence on the corrosion and wear rates was observed in composites mainly due to increased porosity and insufficient matrix/reinforcement bonding.
Descrição
Palavras-chave
Al2O3, CoCrMo, Composite, Corrosion, Hot pressing, Tribocorrosion
Idioma
Inglês
Como citar
Tribology - Materials, Surfaces & Interfaces, v. 8, n. 4, p. 201-208, 2014.