Rugosidade superficial de ligas com alto conteúdo de cobre, em função do aquecimento acima da temperatura de fusão.
Loading...
Date
Advisor
Coadvisor
Graduate program
Undergraduate course
Journal Title
Journal ISSN
Volume Title
Publisher
Type
Article
Access right
Acesso aberto
Abstract
Being the surface roughness a fundamental property in the fit of the castings, it was determined the roughness of 5 high-copper casting alloys, according to the heating over their melting temperature. That way, the specimens made with smooth plastic in the shape of a rectangular plate, 2 mm x 7 mm x 11 mm were invested into a cristobalite investment. After heating and elimination on the plastic, the molds were filled by 3 g of molten alloy, casted in a electrical casting machine at the casting temperature at 25 degrees C and 50 degrees C overheating. The surface roughness was measured in a roughness analyser, Talysurf. As a result, it was verified that there is a variation of surface roughness among the alloys tested, and the heating of the alloys until 50 degrees C over the melting temperature does not interfere in the roughness.
Description
Language
Portuguese
Citation
Revista de Odontologia da UNESP, v. 19, n. 1, p. 203-209, 1990.