Publication: Continuous production of a multi-filament reinforced metal matrix composite strip from the semisolid state
Loading...
Date
Advisor
Coadvisor
Graduate program
Undergraduate course
Journal Title
Journal ISSN
Volume Title
Publisher
Type
Work presented at event
Access right
Acesso aberto
Abstract
Continuous metal matrix composite strip casting (MMCS-ing) composed of six 0.3-mm diameter annealed bare copper wires in a eutectic SnPb matrix was manufactured by a two-roll melt dragged processing (TRMD-ing) method at a rate of 0.3 m/s. The wires were dragged through a semisolid pool with a fibre contact time of approximately 0.2 s. The required gap between rolls to thixoforge the semisolid material around the wire filaments was approximately 1.4 mm. A successful continuous composite strip casting was achieved with a notably good degree of wire alignment. No cracks were observed at the copper wire/matrix interface. However, regions of porosity occurred in the matrix; their possible formation mechanisms are discussed. The solidification structure of the matrix was analysed, and the analysis results indicated the formation of small globular grains measuring approximately 3 µm in diameter. The specimens were evaluated for their tensile properties and compared with the rule of mixtures. The surface fracture analysis indicated a good matrix/fibre union. MMCS-ing is an economically viable process and has significant advantages over other metal matrix composite (MMC) fabrication methods.
Description
Keywords
Metal matrix composites, Metallic fibres, SnPb alloys, Strip casting
Language
English
Citation
Solid State Phenomena, v. 217-218, p. 265-273.