Publicação: High-velocity oxyfuel Cr3C2-NiCr replacing hard chromium coatings
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Asm International
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Comparative wear and corrosion properties of Cr3C2-NiCr (CC-TS) (a high-velocity oxyfuel [HVOF]) and hard chromium (HC) coating's obtained on a steel substrate have been studied. The structural characterization was done before and after measurements by optical microscopy, scanning electron microscopy, and scanning white light interferometry. Wear and corrosion properties were evaluated by ball on disk (ASTM G99-90), rubber wheel (ASTM G65-91), and electrochemical measurements of open circuit and polarization curves. The best corrosion and wear resistance was for the CC-TS obtained by HVOF. The open-circuit potential values measured for both samples after 18 h of immersion we're: -0.240 and -0.550 V, respectively, for CC-TS and HC, versus Ag/AgCl,KClsat. Three orders of magnitude lower volume loss were found for CC-TS (HVOF) after friction tests compared with HC.
Descrição
Palavras-chave
corrosion resistance, Cr3C2-NiCr, hard chromium, high-velocity oxyfuel, thermal spray, wear
Idioma
Inglês
Como citar
Journal of Thermal Spray Technology. Materials Park: Asm International, v. 14, n. 3, p. 335-341, 2005.