Publicação: Assessment of Enamel Bond Strength of Hypoplastic Primary Teeth
Nenhuma Miniatura disponível
Data
2016-09-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Resenha
Direito de acesso
Acesso restrito
Resumo
Purpose: The purpose of this study was to compare the enamel bond strength of hypoplastic and healthy primary teeth. Methods: Twenty-five hypoplastic teeth (experimental group) and 25 healthy primary teeth (control group) were selected and conditioned with 35 percent orthophosphoric acid before a two-layer adhesive system (Single Bond) was applied. Composite resin (Filtek Z350) was inserted in a single application, two-mm high and one-mm in diameter, and then light-cured for 20 seconds. After being stored in distilled water for 24 hours, the specimens were submitted to a shear bond strength test. Fractures were analyzed under a stereomicroscope. Results: No significant differences in bond strength were observed between the experimental group (70.27±20.40 MPa) and control group (67.84±23.37 MPa; P>0.05). However, adhesive fractures were more frequently observed in healthy teeth (72 percent) while hypoplastic teeth presented mixed fractures (60 percent) and enamel cohesive fractures (36 percent). Conclusions: The shear bond strength of the enamel of hypoplastic primary teeth was similar to that of healthy teeth. However, distinct characteristics were observed in the dental samples following fracture.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Pediatric Dentistry, v. 38, n. 5, p. 432-436, 2016.