Heavy metal oxide glass-ceramics containing luminescent gallium-garnets single crystals for photonic applications

Carregando...
Imagem de Miniatura

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Tipo

Artigo

Direito de acesso

Resumo

Glass-ceramics containing rare earth gallium garnets were obtained using glass compositions as reactional medium. This work reports on the synthesis, and structural, morphological, and optical characterizations of Er3+ and Tm3+-doped Yb3Ga5O12 crystals prepared from controlled cooling of heavy metal oxide glass melts. Micrometric cubic crystals were obtained by controlling the cooling of a rare earth-supersaturated glassy composition melted at high temperature. Crystals with sizes ranging between 5 and 150 µm were formed into the glass matrix. A gallium garnet phase corresponding to space group Ia-3d was identified by X-ray diffraction and confirmed by Rietveld simulations. The morphology of crystals was studied by optical and scanning electron microscopies, while chemical elements were mapped by electron dispersive X-Ray spectroscopy. The glass phase was studied by XRD, thermal analysis and Raman spectroscopy. The optical properties of both glass and glass-ceramic materials were evaluated by UV–Vis and luminescence spectroscopies. Micro-luminescence measurements confirmed that rare earths were incorporated into the crystalline phase. Intense upconversion emissions of Er3+ (550 and 660 nm) and Tm3+ (800 nm) were observed when the glass-ceramics were pumped at 980 nm. These new glass-ceramics are excellent candidates for the development of photonic devices.

Descrição

Palavras-chave

Gallium garnet, Glass matrix composites, Glass-ceramics, Luminescence, Rare earths

Idioma

Inglês

Como citar

Journal of Alloys and Compounds, v. 864.

Itens relacionados

Unidades

Unidade
Instituto de Química
IQAR
Campus: Araraquara


Departamentos

Cursos de graduação

Programas de pós-graduação