Show simple item record

dc.contributor.authorNascimento, M. P.
dc.contributor.authorVoorwald, HJC
dc.contributor.authorSouza, R. C.
dc.contributor.authorPigatin, W. L.
dc.identifier.citationPlating and Surface Finishing. Orlando: Amer Electroplaters Soc Inc., v. 88, n. 4, p. 84-90, 2001.
dc.description.abstractDespite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental requirements causes one to search for possible alternatives. To improve the fatigue and corrosion resistance of AISI 4340 steel, an experimental study has been made for an intermediate electroless nickel layer deposited on base metal. The objective of this study was to analyze the effect of nickel underplate on the fatigue and corrosion strength of hard-chromium-plated AISI 4340 steel. Deposition of the conventional wear-resistant hard chromium plating leads to a decrease in mechanical properties of the base metal, especially the fatigue strength. Rotating bending fatigue tests results indicate better performance for conventional hard chromium plating. Good corrosion resistance in salt fog exposure was obtained for the accelerated hard chromium plating. Experimental data showed higher fatigue and corrosion resistance for samples prepared with accelerated hard chromium plate over electroless nickel plate, when compared with samples without electroless nickel underplate.en
dc.publisherAmer Electroplaters Soc Inc
dc.relation.ispartofPlating and Surface Finishing
dc.sourceWeb of Science
dc.titleEvaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steelen
dcterms.rightsHolderAmer Electroplaters Soc Inc
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.contributor.institutionUniversidade de São Paulo (USP)
dc.description.affiliationSão Paulo State Univ, Mat & Technol Dept, FEG, São Paulo, Brazil
dc.description.affiliationFAENQUIL, DEMAR, Chem Engn Fac, Dept Mat, Lorena, SP, Brazil
dc.description.affiliationEMBRAER, LIEBHERR, EDE, Equipment Div, Sao Jose Dos Campos, Brazil
dc.description.affiliationUnespSão Paulo State Univ, Mat & Technol Dept, FEG, São Paulo, Brazil
dc.rights.accessRightsAcesso restrito
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Engenharia, Guaratinguetápt
Localize o texto completo

Files in this item


There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record