Preparation and characterization of glass-ceramic materials in the BaO-Li2O-ZrO2-SiO2 system and their dependence on treatment temperatures
Nenhuma Miniatura disponível
Data
1999-07-01
Autores
Silveira, Cristian Berto da
Campos, Silvia Denofre de
Castro, Sandra C. de
Kawano, Yoshio
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
The preparation and characterization of transparent glass-ceramics in the composition of 30Li2O:5ZrO2:xBaO:(100-x) SiO2 with x = 0, 5, 10, 15, and 20 mol% are described. Glasses were melted in a platinum crucible at 1100°C for 2 h and then heat-treated at 900°C for 3 h. The characterizations were performed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman and infrared spectroscopy, and scanning electron microscopy (SEM). The experimental results indicate that there was a structural change in the glass-ceramics as the BaO concentration in the mixture increased. In the XRD patterns of samples without heat treatment, only the halo was observed. After heat treatment, the appearance of the materials was verified by X-ray diffraction peaks. The reorganization of the amorphous solid was confirmed by Raman and IR spectroscopy along with XPS and SEM, with a more homogeneous phase formation being observed.
Descrição
Palavras-chave
Composition, Glass, High temperature operations, Infrared spectroscopy, Melting, Oxides, Phase transitions, Raman spectroscopy, Scanning electron microscopy, Thermal effects, X ray diffraction analysis, X ray photoelectron spectroscopy, Glass ceramic materials, Halo, Structural change, Ceramic materials
Como citar
Materials Research Bulletin, v. 34, n. 10-11, p. 1661-1671, 1999.