Magnetic properties of spindle-type iron fine particles obtained from hematite

Nenhuma Miniatura disponível

Data

2001-12-01

Autores

Varanda, L. C. [UNESP]
Jafelicci, M. [UNESP]
Goya, G. F.

Título da Revista

ISSN da Revista

Título de Volume

Editor

Resumo

Spindle-type iron fine particles have been prepared by reduction of silica-coated-hematite particles. Hydrogen reduction of the coated-hematite cores yielded uniform spindle-type iron particles, which were stabilized by surface oxidation. Narrow particle distributions are observed from TEM measurements. X-ray, Mössbauer and magnetization data are in agreement with the presence of nanosized α-Fe particles, having surface layer of spinel structure oxide. Mössbauer spectra show that the oxide surface is superparamagnetic at room temperature. © 2001 Elsevier Science B.V. All rights reserved.

Descrição

Palavras-chave

Fine particles, Iron particles, Magnetic pigments, Magnetic recording media, Hematite particles, Hydrogen reduction, Iron-fines, Magnetization data, Mossbauer, Nano-sized, Oxide surface, Particle distributions, Room temperature, Silica-Coated, Spinel structure, Superparamagnetics, Surface layers, Surface oxidations, TEM, Hematite, Iron ores, Magnetic devices, Magnetic properties, Magnetic recording, Magnetism, Molybdenum oxide, Reaction kinetics, Silica, Superparamagnetism, Surface structure, Magnetic bubbles

Como citar

Journal of Magnetism and Magnetic Materials, v. 226-230, n. PART II, p. 1933-1935, 2001.