Effects of reducing light-curing time of a high-power LED device on shear bond strength of brackets

Carregando...
Imagem de Miniatura

Data

2018-09-01

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Urban & Vogel

Tipo

Artigo

Direito de acesso

Acesso abertoAcesso Aberto

Resumo

Purpose To assess the effects of reducing the curing time of a high-power light-emitting diode (LED) unit (Valo, Ultradent, South Jordan, UT, USA) on shear bond strength (SBS) of metal brackets and on the amount of adhesive remnant of two orthodontic composites. Methods Eighty human premolars were divided into four groups (G1-4) according to curing time and composite: G1 (Transbond XT, 6s), G2 (Opal Bond MV, 6s), G3 (Transbond XT, 3s), and G4 (Opal Bond MV, 3s). Twenty-four hours after bonding, brackets were subject to a SBS test performed with a universal testing machine. Enamel surface was analyzed by SEM and the amount of adhesive remnant was assessed by the Image J software area calculation tool. Two-way analysis of variance was used for statistical analysis of SBS data, while Friedman and Mann-Whitney post hoc tests were used to analyze data on the amount of adhesive remnant. Results Time and composite significantly affected SBS (p<0.001). The 6s curing showed a higher SBS value (21.56 MPa) in comparison to 3s curing (15.79 MPa). Transbond XT composite showed a significantly higher SBS value (21.06 MPa) compared to Opal Bond MV (16.29 MPa). After the SBS test, Opal Bond MV showed a significantly greater amount of composite adhered to enamel (p<0.001). Conclusion Reducing exposure time from 6 to 3s significantly decreased mean values of SBS, even with the use of a high-power LED unit. Reduction in time did not affect the amount of adhesive remnant.

Descrição

Idioma

Inglês

Como citar

Journal Of Orofacial Orthopedics-fortschritte Der Kieferorthopadie. Munich: Urban & Vogel, v. 79, n. 5, p. 352-358, 2018.

Itens relacionados

Financiadores