Efeito da aplicação de carga em coroas de diferentes materiais, confeccionadas sobre implantes unitários curtos e com diferentes diâmetros nas deformações da crista óssea : análise in vitro e in silico

dc.contributor.advisorNogueira Junior, Lafayette
dc.contributor.authorMonteiro, Fabricio Malheiros de Miranda
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2018-07-18T18:10:35Z
dc.date.available2018-07-18T18:10:35Z
dc.date.issued2018-06-25
dc.description.abstractO intuito deste estudo in vitro e in silico, foi analisar as microdeformações, geradas pela aplicação de carga vertical, sobre coroas de 3 tipos de materiais restauradores diferentes (Zircônia, Dissilicato de Lítio e Cromo Cobalto), que foram selecionadas, através da biblioteca do software SMART DENT/Exocad (Darmstadt - Germany) e confeccionadas, através da tecnologia cad/cam, suportadas por implantes curtos (8mm), conexão cone morse, com diversos diâmetros (3,5 mm; 4,0 mm e 5,0 mm). Os implantes foram instalados 2mm infraósseo para análise através de elementos finitos e da extensometria. Foram confeccionados 3 blocos de poliuretano: bloco 1 (grupo experimento) no qual foi colocado um implante Titamax CM Neodent 3,5 X 08 mm, bloco 2 (grupo controle) no qual foi colocado um implante titamax CM Neodent 4,0 X 08 mm e bloco 3 (grupo controle) no qual foi colocado um implante titamax CM Neodent 5,0 X 08 mm. Pilares protéticos retos (Base de Titânio 4,5 - Neodent) foram instalados sobre os respectivos implantes sendo instalados 4 extensômetros, na região superior dos blocos ao redor dos implantes. Foi aplicada uma carga vertical de 300N ao redor da abertura de acesso do parafuso protético das coroas. Para a análise por elementos finitos (FEA), o mesmo bloco foi modelado e analisado sob a mesma carga de 300N. Os valores de tensão e deformação foram analisados quanto à correlação com a extensometria. A estatística inferencial consistiu no teste de análise de variância de Friedmann, um fator efeito fixo. Para o nível de significância, foi escolhido o valor convencional de 5%. Os resultados demonstraram haver diferença estatística significante para o fator diâmetro (p = 0,0001) no qual os implantes, com 3,5 mm de diâmetro apresentaram os maiores picos de microdeformações. Quando se analisa o material restaurador, observa-se que não houve diferenças estatísticas significativas (p = 0,783). Dentro das limitações deste estudo, pode-se concluir que a utilização de implantes unitários, curtos e estreitos com conexão cone morse instalados 2 mm infraósseo, são uma opção viável para reabilitações em regiões posteriores independente do material restaurador escolhido.pt
dc.description.abstractThe aim of this in vitro and in silico study was to analyze the microdeformations generated by the application of vertical load on crowns of 3 different types of restorative materials (Zirconia, Lithium Dissilicate and Cobalt Chromium) that were selected through the software library SMART DENT / Exocad (Darmstadt - Germany), and made using cad / cam technology, supported by short implants (8 mm), cone morse connection with various diameters (3.5 mm, 4.0 mm and 5.0 mm). These were installed 2 mm subcrestal for finite element analysis and extensometry. Three blocks of polyurethane were made; block 1 (experimental group) in which a Titamax CM Neodent 3.5 X 08 mm implant, block 2 (control group) was implanted in which a CM Neodent 4.0 X 08 mm titamax and block 3 (control group) were implanted in which an implant was placed titamax CM Neodent 5.0 X 08 mm. Straight prosthetic abutments (Titanium Base 4.5 - Neodent) were installed on the respective implants and 4 extensometers were installed, in the upper region of the blocks around the implants. A vertical load of 300N was applied around the access opening of the crown prosthetic screw. For the finite element analysis (FEA), the same block was modeled and analyzed under the same 300N load. The stress and strain values were analyzed for correlation with extensometry. The inferential statistics consisted of Friedmann's analysis of variance, a fixed effect factor. For the level of significance, the conventional value of 5% was chosen. The results showed a statistically significant difference for the diameter factor (p = 0.0001) where 3.5 mm diameter implants presented the highest peaks of microdeformations. When analyzing the restorative material, we observed that there were no significant statistical differences (p = 0.783). Within the limitations of this study, we can conclude that the use of short, narrow unit implants with cone morse connection installed 2 mm subcrestal are a viable option for rehabilitation in posterior regions independent of the restorative material chosen.en
dc.identifier.aleph000906033
dc.identifier.capes33004145070P8
dc.identifier.lattes7376974788169619
dc.identifier.orcid0000-0001-8443-6722
dc.identifier.urihttp://hdl.handle.net/11449/154540
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subjectDissilicato de Lítiopt
dc.subjectLigas de Cromopt
dc.subjectZircôniapt
dc.subjectImplantes curtospt
dc.subjectImplantes estreitospt
dc.subjectLithium Dissilicateen
dc.subjectCromo leadsen
dc.subjectZirconiaen
dc.subjectShort implantsen
dc.subjectNarrow implantsen
dc.titleEfeito da aplicação de carga em coroas de diferentes materiais, confeccionadas sobre implantes unitários curtos e com diferentes diâmetros nas deformações da crista óssea : análise in vitro e in silicopt
dc.title.alternativeEffect of the load application on crowns of different materials made on short unitary implants with different diameters in bone crest deformations : in vitro and in silico analysispt
dc.typeDissertação de mestrado
unesp.advisor.lattes7376974788169619
unesp.advisor.orcid0000-0001-8443-6722
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargoOnlinept
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesempenho de materiais reabilitadores protéticospt

Arquivos

Pacote Original

Agora exibindo 1 - 1 de 1
Carregando...
Imagem de Miniatura
Nome:
monteiro_fmm_me_sjc.pdf
Tamanho:
2.13 MB
Formato:
Adobe Portable Document Format
Descrição:

Licença do Pacote

Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.12 KB
Formato:
Item-specific license agreed upon to submission
Descrição: