Estudo da influência das adições de fibra de vidro álcali-resistentes nas propriedades do concreto permeável

Página do item simplificado
dc.contributor.advisorAlbuquerque, Maria da Consolação Fonseca de [UNESP]
dc.contributor.authorSantana, Anderson Mauricio Carvalho
dc.date.accessioned2024-06-11T11:17:01Z
dc.date.available2024-06-11T11:17:01Z
dc.date.issued2024-02-29
dc.description.abstractA impermeabilização do solo tem consequências negativas para a drenagem urbana. Sem a capacidade de absorção natural do solo, a água da chuva não consegue escoar adequadamente, resultando em alagamentos e enchentes. Além disso, a drenagem urbana inadequada também contribui para a poluição dos corpos d'água, pois leva consigo uma grande quantidade de resíduos sólidos e poluentes presentes nas ruas e calçadas. O concreto permeável surgiu como forma de mitigar os problemas. No presente trabalho, foram confeccionadas misturas de concreto permeável utilizando traço de 1:4,6, com 10% de sílica, 0,5% de aditivo superplastificante em relação ao peso do cimento e adicionou-se 0,34% (em relação ao cimento) de água para reação do cimento e absorção do agregado. Nessas misturas foi adicionado o percentual de 10% e 20%, em relação a massa total do traço, de fibra de vidro álcali-resistente (AR). As fibras de vidro AR são fibras resistentes as propriedades químicas e agressivas do concreto. Procurou-se observar a influência de adição das fibras nas propriedades mecânicas das misturas. Para isso foram realizados os ensaios de: resistência à compressão axial, tração por compressão diametral, flexão a três pontos, massa específica, índice de vazios e coeficiente de permeabilidade. Observou-se que o acréscimo de fibra de vidro AR causou queda na resistência à compressão axial na mistura com adição de 10% e 20% de fibra de vidro AR. Notou-se que ao adicionar 10% de fibra de vidro AR na mistura, a resistência a compressão diametral aumentou em comparação com a mistura de referência, sem essa fibra. Constatou-se que a mistura com adição de 10% de fibra de vidro AR obteve a maior resistência à flexão com um aumento de 24% em relação à mistura de referência. A massa específica seca da mistura com adição de 10% e 20% de fibra de vidro AR diminui em relação ao valor da mistura de referência. Também foi observado um aumento no índice de vazios nas misturas com a adição de 10% e 20% de fibras de vidro AR. Entretanto, reduziu o coeficiente de permeabilidade em comparação com a mistura de referência.pt
dc.description.abstractSoil waterproofing has negative consequences for urban drainage. Without the soil's natural absorption capacity, rainwater is unable to drain properly, resulting in flooding and floods. In addition, inadequate urban drainage also contributes to the pollution of water bodies, as it carries a large amount of solid waste and pollutants present on the streets and sidewalks. Permeable concrete has emerged as a way to mitigate these problems. In this study, mixes of permeable concrete were made using a ratio of 1:4.6, with 10% silica, 0.5% superplasticizer additive in relation to the weight of the cement and 0.34% water (in relation to the cement) added for cement hydration and aggregate absorption. In these mixes, 10% and 20% of alkali-resistant fiberglass (AR) were added in relation to the total weight of the mix. AR fiberglass is resistant to the chemical and aggressive properties of concrete. The influence of adding fibers on the mechanical properties of the mixes was observed by conducting tests such as axial compression strength, compressive tensile strength, three-point bending, specific gravity, void content, and permeability coefficient. It was noted that the addition of AR fiberglass caused a decrease in axial compression strength in the mix with 10% and 20% of AR fiberglass. It was observed that adding 10% of AR fiberglass to the mix increased compressive tensile strength compared to the reference mix without this fiber. The mix with 10% AR fiberglass added obtained the highest bending strength with a 24% increase compared to the reference mix. The dry specific gravity of the mix with 10% and 20% added AR fiberglass decreased compared to the value of the reference mix. An increase in void content was also observed in the mixes with the addition of 10% and 20% of AR fiberglass. However, the permeability coefficient decreased compared to the reference mix.en
dc.identifier.citationSANTANA, Anderson Mauricio Carvalho. Estudo da influência das adições de fibra de vidro álcali-resistentes nas propriedades do concreto permeável. 2024. 102 f. Dissertação (Mestrado em Engenharia Civil) - Faculdade de Engenharia, Universidade Estadual Paulista - UNESP, Ilha Solteira, 2024.
dc.identifier.urihttps://hdl.handle.net/11449/255919
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso restrito
dc.subjectConcreto permeávelpt
dc.subjectResistênciapt
dc.subjectPermeabilidadept
dc.subjectFibra de vidro arpt
dc.subjectPermeable concreteen
dc.subjectStrengthen
dc.subjectPermeabilityen
dc.subjectAr glass fiberen
dc.titleEstudo da influência das adições de fibra de vidro álcali-resistentes nas propriedades do concreto permeável
dc.title.alternativeStudy of the influence of alkali-resistant fiberglass additions on the properties of permeable concreteen
dc.typeDissertação de mestradopt
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Engenharia, Ilha Solteirapt
unesp.embargo6 meses após a data da defesa
unesp.examinationboard.typeBanca pública
unesp.graduateProgramCiência dos Materiais - FEIS 33004099083P9
unesp.knowledgeAreaEstruturas e materiais
unesp.researchAreaNão consta

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
santana_amc_me_ilha.pdf
Tamanho:
2.83 MB
Formato:
Adobe Portable Document Format
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
2.14 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Ilha Solteira - FEIS - Faculdade de Engenharia