Análise das tensões geradas durante a contração de polimerização e aplicação de cargas em restaurações diretas de resina composta. Efeito da utilização de materiais para base ou forramento

Página do item simplificado
dc.contributor.advisorDuarte Junior, Sillas Luiz Lordelo [UNESP]
dc.contributor.advisorDinelli, Welingtom [UNESP]
dc.contributor.authorOliveira, Luana Cristina Araújo de [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:31:26Z
dc.date.available2014-06-11T19:31:26Z
dc.date.issued2004-06-26
dc.description.abstractO objetivo desta investigação científica foi analisar o efeito da presença de materiais para base ou forramento, nas tensões geradas durante a contração de polimerização e aplicação de cargas, em cavidade classe I, no segundo pré-molar superior. Foram avaliadas quatro técnicas restauradoras: 1) Resina composta Z250(3M ESPE) controle, 2) Resina composta Z250(3M ESPE) + forramento com resina de baixa viscosidade FiltekFlow(3M ESPE), 3) Resina composta Z250(3M ESPE) + Forramento com ionômero de vidro modificado por resina Vitrebond(3M ESPE) e 4) Resina composta Z250(3M ESPE) + base com ionômero de vidro modificado por resina Vitrebond(3M ESPE). O estudo transcorreu em três fases: 1)Fotoelasticidade, 2)Tensilometria e 3)Elementos Finitos. 1ª Fase (Fotoelasticidade) - Nesta etapa foram avaliadas as tensões geradas durante a contração de polimerização na cavidade confeccionada em modelo fotoelástico, restaurada com as técnicas descritas acima, nomeadas F1, F2, F3 e F4 respectivamente e determinada a Tensão Cisalhante Máxima(tmáx ) na interface adesiva e realizados os Testes ANOVA e Tukey (p=0,05). 2ª Fase (Tensilometria) - Nesta etapa foram avaliadas as tensões geradas durante a contração de polimerização de cada material, assim agrupados: T1 - resina composta, T2 - resina de baixa viscosidade e T3 - Ionômero de vidro modificado por resina, os quais foram inseridos entre duas bases cilíndricas de dentina bovina (diâmetro 4,0 mm) com espessura de 2,0mm, sendo que a base superior foi conectada a uma célula de carga. Os valores de força foram registrados iniciando simultaneamente com a fotopolimerização até a completa estabilização das forças...pt
dc.description.abstractThe aim of this study was analyze the effect of liner and base materials presence during polymerization shrinkage and load application, on cavities class I, in maxillary premolar. The following technique were assigned: 1) Composite resin Z250(3M ESPE)-control, 2) Composite resin Z250(3M ESPE) + liner with flowable FiltekFlow (3M ESPE) 3) Composite resin Z250(3M ESPE) + liner with resin-modified glass-ionomer Vitrebond(3M ESPE) e 4) Composite resin Z250(3M ESPE) + base with resin-modified glass-ionomer Vitrebond(3M ESPE). The study was divided in three phases: 1) Photoelasticity, 2) Tensilometry e 3) Finite Elements Analysis. 1ª (Photoelasticity) - In this phase was determinate polymerization shrinkage stress in photoelastic model, filled with techniques, named F1, F2, F3 e F4 respectively and Maximal Shear Stress (tmáx) was determinate along adhesive interface. Results were analyzes by Anova and Tukey Test. (p=0,05). 2ª (Tensilometry) - In this phase was determinate, polymerization shrinkage stress, for each material: T1 - composite resin, T2 - flowable resin e T3 - resin-modified glass-ionomer. Materials were inserted into 2mm space, between two dentin bovine cylindrical bases, (diameter 4,0mm), which one was connected a load cell. A curve ForceXTime, was obtained for each of samples. Results were analyzes by Anova and Tukey Test. (p=0,05). 3ª (Finite Elements Analysis) - In this phase, stresses resulting from polymerization shrinkage in combination with oclusal loading, were determinate in a 2D finite element model. The polymerization shrinkage stress was fundamented in Tensilometry and Phoelasticity results... (Complete abstract, click electronic access below)en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent234 f. : il.color.
dc.identifier.aleph000498267
dc.identifier.capes33004030010P2
dc.identifier.citationOLIVEIRA, Luana Cristina Araújo de. Análise das tensões geradas durante a contração de polimerização e aplicação de cargas em restaurações diretas de resina composta. Efeito da utilização de materiais para base ou forramento. 2004. 234 f. Tese (doutorado) - Universidade Estadual Paulista, Faculdade de Odontologia de Araraquara, 2004.
dc.identifier.fileoliveira_lca_dr_arafo.pdf
dc.identifier.urihttp://hdl.handle.net/11449/101374
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectForramento da cavidade dentáriapt
dc.subjectResinas compostaspt
dc.subjectCimentos de ionômeros de vidropt
dc.subjectComposites resinen
dc.subjectGlass ionomer cementsen
dc.subjectDental cavity liningen
dc.titleAnálise das tensões geradas durante a contração de polimerização e aplicação de cargas em restaurações diretas de resina composta. Efeito da utilização de materiais para base ou forramentopt
dc.typeTese de doutorado
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Odontologia, Araraquarapt
unesp.graduateProgramCiências Odontológicas - FOARpt
unesp.knowledgeAreaDentística restauradorapt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
oliveira_lca_dr_arafo.pdf
Tamanho:
2.17 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Teses - Ciências Odontológicas - FOAR