Resistência de união ao push-out entre resina e dentina radicular: Efeito utilização da solução irrigadora antes da cimentação do pino
Nenhuma Miniatura disponível
Data
2017-01-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Objective: To evaluate the effect of different irrigation solutions prior to post cementation on the resin bonding to bovine root dentine. Material and Methods: 60 bovine roots (16 mm) were prepared to 12 mm with specific drill of a double-tapered fiber post system, included in PMMA, and divided into 6 groups, considering the irrigation solutions (IS) prior to cementation: Gr1- saline solution (control), Gr2- NaOCl 0.5 %, Gr3- NaOCl 1 %, Gr4- NaOCl 2.5 %, Gr5- NaOCl 5 %, Gr6- Chlorexidine 2 % (solution). The root canals were irrigated with IS 20 ml during 10 min. Then they were rinsed with 20 ml of distilled water and dried with paper points. One fiber post was molded with polyvinylsiloxane and 60 posts made of resin cement (PRC) were obtained moments before the cementation. The root canal dentin was etched with H2PO3 37 %/15 s + washing/drying, a multi-bottle etch&rinse adhesive system was applied and the PRC were resin luted with dual resin cement (DuolinkTM, Bisco). Each specimen was cut into 4 slices of ±1.8mm in thickness and submitted to push-out test (1 mm/min). Results: ANOVA showed that bond strength was significantly affected by IS (P<0.0001). The highest bond strengths (MPa) were those for the groups 4 (3.51 ± 1.52) and 5 (3.0 ± 1.16). The groups 1 (0.70 ± 0.30), 2 (0.80 ± 0.24), 3 (1.26 ± 0.57) and 6 (0.90 ± 0.41) were statistically similar to each other. Conclusion: The resin bonding to the root dentine was higher when higher concentrations of hypochlorite solutions were used.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Brazilian Dental Science, v. 20, n. 2, p. 85-92, 2017.