Nanoscale polarization relaxation and piezoelectric properties of SBN thin films
Nenhuma Miniatura disponível
Data
2016-01-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Ieee
Tipo
Trabalho apresentado em evento
Direito de acesso
Acesso aberto
Resumo
Randomly oriented Sr0.75Ba0.25Nb2O6 thin films have been deposited on Pt(111)/Ti/SiO2/Si substrates using a polymeric chemical route to study their peculiar nanopolar structures and local ferroelectric properties using piezoresponse force microscopy (PFM) technique. PFM images reveals grains with contrast among fully white and fully black, a clear indication of non-zero polarization in the SBN films far above T-m similar to 221 K. Asymmetries observed in local hysteresis loops recorded at different grains suggest an imprint effect in the studied films due to an internal build-in electric field. Some grains show asymmetric hysteresis loops while other grains show symmetric hysteresis loops. The origin of the imprint effect observed in the SBN films is discussed in terms of complex defects associated to oxygen vacancies. The experimental relaxation curves were fitted using the Kohlrausch-Williams-Watts function. The time constant tau increases from 404 to 977 ms as the magnitude voltage increases.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
2016 Joint Ieee International Symposium On The Applications Of Ferroelectrics, European Conference On Application Of Polar Dielectrics, And Piezoelectric Force Microscopy Workshop (isaf/ecapd/pfm). New York: Ieee, 4 p., 2016.