Sintering and crystallite growth of nanocrystalline copper doped tin oxide

dc.contributor.authorSantilli, Celso Valentim [UNESP]
dc.contributor.authorPulcinelli, Sandra Helena [UNESP]
dc.contributor.authorBrito, GES
dc.contributor.authorBriois, V
dc.contributor.institutionCtr Univ Paris Sud
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-05-20T15:23:16Z
dc.date.available2014-05-20T15:23:16Z
dc.date.issued1999-04-08
dc.description.abstractThe effect of Cu2+ contents and of firing temperature on sintering and crystallite growth of nanocrystalline SnO2 xerogels was analyzed by thermoanalysis (mass loss (TG), linear shrinkage, and differential thermal analysis (DTA)), X-ray powder diffraction (XRPD), and EXAFS (extended X-ray absorption fine structures) measurements. Samples were prepared by two methods: (a) coprecipitation of a colloidal suspension from aqueous solution containing both Sn(IV) and Cu(II) ions and (b) grafting copper(II) species on the surface of tin pride gel. The thermoanalysis has shown that the shrinkage associated with the mass loss decreases by increasing the amount of copper. The EXAFS measurements carried out at the Cu K edge have evidenced the presence of copper in substitutional solid solution for the dried xerogel prepared with 0.7 mol % of copper, while for higher concentration of doping, copper has been observed also at the external surface of crystallites. The solid solution is metastable and copper migrates toward the surface during firing. The XRPD and DTA results have shown a recrystallization process near 320 degrees C, which leads to crystallite growth. The presence of copper segregated near the crystallite surface controls its growth.en
dc.description.affiliationCtr Univ Paris Sud, LURE, F-91898 Orsay, France
dc.description.affiliationUNESP, Inst Quim, BR-14801970 Araraquara, SP, Brazil
dc.description.affiliationUnespUNESP, Inst Quim, BR-14801970 Araraquara, SP, Brazil
dc.format.extent2660-2667
dc.identifierhttp://dx.doi.org/10.1021/jp984129v
dc.identifier.citationJournal of Physical Chemistry B. Washington: Amer Chemical Soc, v. 103, n. 14, p. 2660-2667, 1999.
dc.identifier.doi10.1021/jp984129v
dc.identifier.issn1089-5647
dc.identifier.lattes5584298681870865
dc.identifier.lattes9971202585286967
dc.identifier.orcid0000-0002-8356-8093
dc.identifier.urihttp://hdl.handle.net/11449/34091
dc.identifier.wosWOS:000079837800013
dc.language.isoeng
dc.publisherAmer Chemical Soc
dc.relation.ispartofJournal of Physical Chemistry B
dc.rights.accessRightsAcesso restrito
dc.sourceWeb of Science
dc.titleSintering and crystallite growth of nanocrystalline copper doped tin oxideen
dc.typeArtigo
dcterms.licensehttp://pubs.acs.org/paragonplus/copyright/jpa_form_a.pdf
dcterms.rightsHolderAmer Chemical Soc
unesp.author.lattes9971202585286967
unesp.author.lattes5584298681870865[1]
unesp.author.orcid0000-0002-8356-8093[1]
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Química, Araraquarapt

Arquivos

Licença do Pacote

Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
1.71 KB
Formato:
Item-specific license agreed upon to submission
Descrição: