Digital smile designing, pressing and stratifying ceramic lithium disilicate veneers to rehabilitate dental agenesis: a clinical report

Abstract

This article had the objective of reporting a case of aesthetic rehabilitation with laminated facets from the 14 to the 24 teeth made with IPS E.max Ceram ceramics (Ivoclar-Vivadent), which replaced previous unsatisfactory composite resin restorations in the anterior region. The patient had agenesis of 12 and 22 teeth, making it necessary to anatomize the anterior teeth. A digital smile design was first virtually created and then followed by a diagnostic wax-up. The following was performed in a single day: periodontal surgery using the flapless technique to achieve prosthetic space; teeth preparation; an additionalsilicone impression; and multiple provisional restorations of bis-acryl composite resins were fabricated. Fourteen days later, in the second session the ceramic veneers were etched with 5% hydrofluoric acid for 20s; they received a silane application and a silane heat treatment, then lastly an ultrasonic bath. A universal adhesive was used in combination with a light curing cement.Cementation was performed immediately following an occlusal adjustment. The patient returned for a follow-up appointment another fourteen days after the luting process, in which a further occlusal adjustment was performed, and he reported complete satisfaction with the treatment.

Este é um relato de caso de reabilitação estética anterior com facetas laminadas dos elementos 14 ao 24 confeccionadas com a cerâmica IPSE.max Ceram (Ivoclar -Vivadent), as quais substituíram facetas de resina composta insatisfatórias dos elementos 13 ao 23. Ressalta-se que o paciente possuía agenesia dos elementos 12 e 22, tornando-se necessária a reanatomização dos dentesanteriores. Inicialmente ocorreu o planejamento digital, seguido pelo enceramento diagnóstico. Foi realizado em consulta única: cirurgia periodontal pela técnica “flapless” para conquista de espaço protético; confecção dos preparos para facetas; moldagem com silicona de adição; e confecção de múltiplos provisórios em resina bisacrilica. Na consulta de cimentação, as peças foram tratadas comácido fluorídrico 5% por 20s; silanizadas com Relyxceramic primer (3M ESPE), submetidas ao tratamento térmico; e banho ultrassônico. O sistema adesivo utilizado foi o Single Bond (3M ESPE) associado ao RelyxVenner (3M ESPE). Imediatamente a cimentação foi realizado um ajuste oclusal. Após 14 dias o paciente retornou para uma nova consulta de acompanhamento, na qual foi realizada mais um ajuste oclusal, e relatou total satisfação com o tratamento realizado.