Publicação: Water as Veneering Modeling Liquid Affects Microhardness of Glassy Matrix Veneering Ceramic
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Resumo
Purpose/Aim: To evaluate the effect of different veneering liquids used for modeling on microhardness, fracture toughness and biaxial flexural strength of a glass-veneering ceramic. Material and methods: The manufacturer recommended modeling liquid (ML), distilled water (DW), isopropyl alcohol (IA), 0.5% (P05), 1% (P1), and 2% (P2) polyethylene glycol solutions were mixed with feldspathic ceramic powder to form disc-shaped samples (n=20, 15 mm × 1.2 mm). After sintering, samples were mirror-polished and subjected to Vickers indentation (n=5) for measurement of microhardness and fracture toughness. The remaining 15 samples from each group were subjected to biaxial flexural strength. Data were subjected to one-way ANOVA and Weibull analysis. Results: The microhardness was affected by veneering liquid (p=0.002): DW promoted higher microhardness values than ML and IA. Fracture toughness (p=0.301) and flexural strength (p=0.930) were not affected by the veneering liquid but Weibull parameters were affected. All groups presented surface pores under high magnification. Conclusion: Even though the use of DW led to higher values of surface microhardness than the ML, all obtained values are inside the range of enamel microhardness values reported in the literature. Such parameters may affect an-tagonist wear and should be reported in clinical trials.
Descrição
Palavras-chave
Modeling Liquid, Polyethylene Glycol, Porcelain
Idioma
Inglês
Como citar
European Journal of Prosthodontics and Restorative Dentistry, v. 30, n. 4, p. 262-266, 2022.