Publicação: Photo-induced electrical behavior under gas adsorption on SnO2 -based heterostructures
Nenhuma Miniatura disponível
Data
2020-11-15
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Resumo
Er-doped SnO2 thin films are produced by a combined technique where films are deposited by resistive evaporation from a precursor powder obtained by sol-gel. Films are deposited on different substrates and analyzed concerning the electrical conduction on different directions. The film conductivity (parallel to the surface) changed significantly when exposed to light, even though the photon energies are below the SnO2 bandgap energy (InGaN LED, 2.75 eV). The SnO2 films present distinct trapping characteristics when exposed to oxygen or carbon monoxide, in agreement with the behavior of metallic oxides, suggesting that surface defects act as adsorption sites. The photo-excitation is rather lower for a GaAs/SnO2 heterostructure sample where the GaAs layer is deposited by sputtering, since the direction of polarization (through the interface barrier, perpendicular to the sample surface) does not lead to significant increase in the sample current. When the bottom layer is a GaAs crystal wafer, the current magnitude increases drastically under the InGaN LED excitation. The results reported here contribute to the understanding of electrical transport and the influence of gas adsorption on evaporated SnO2 films deposited in diverse configurations on distinct substrates, and contributes to gas sensing applications.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Materials Chemistry and Physics, v. 255.