Shear bond strength between metal alloy and a ceramic system, submitted to different thermocycling immersion times.
Loading...
Date
Advisor
Coadvisor
Graduate program
Undergraduate course
Journal Title
Journal ISSN
Volume Title
Publisher
Type
Article
Access right
Abstract
The aim of this study was to evaluate the shear bond strength of Co-Cr and Ni-Cr metal alloys and a specific ceramic, submitted to different thermocycling immersion times. Sixty metal-ceramic specimens were confectioned and standardized in cylindricalformat. Three thermocycling conditions were evaluated: without thermocycling, 3,000 cycles (5 degrees C/55 degrees C+/-1) with 30s of immersion time and 3,000 cycles (5 degrees C/55 degrees C+/-1) with 60s. The shear bond strength was performed in a universal testing machine, using a special device to concentrate the tension at the metal/ceramic interface during the test. The load was applied until fracture of the specimens. The data was statistically analyzed by ANOVA (two-way) and Tukey (p<0.05) test. The results didn't show significant statistic differences between the metal-porcelain combinations. Nevertheless, both metal-ceramic systems submitted to 60s of immersion time showed lower values compared to specimens without thermocycling. It was concluded that the thermocycling immersion time of 1 minute affect the shear bond strength values for the Ni-Cr/porcelain and Cr-Co/porcelain systems.
Description
Keywords
Language
English
Citation
Acta odontológica latinoamericana : AOL, v. 20, n. 2, p. 97-102, 2007.
Related itens
Sponsors
Other forms of access