Publication: Estudo das propriedades elétro-óptica de dispositivos eletroluminescentes confeccionados com um compósito híbrido
Loading...
Date
Authors
Advisor
Chinaglia, Dante Luis 
Coadvisor
Graduate program
Física - IGCE
Undergraduate course
Journal Title
Journal ISSN
Volume Title
Publisher
Universidade Estadual Paulista (Unesp)
Type
Master's thesis
Access right
Acesso aberto
Abstract
Abstract (portuguese)
Neste trabalho foi desenvolvido um dispositivo eletroluminescente (EL) constituído de um compósito híbrido (CH), formado por uma blenda polimérica e um material EL inorgânico. A blenda é composta por um polímero condutor, a poli(o-metoxianilina) (POMA) dopada com ácido tolueno sulfônico (TSA), e um polímero isolante, o poli(fluoreto de vinilideno-co-trifluoretileno) (P(VDF-TrFE)). A esta blenda é acrescentado um material EL inorgânico, o silicato de zinco dopado com Manganês (Zn2SiO4:Mn), formando assim, o compósito híbrido. O dispositivo foi construído depositando o compósito por drop casting sobre um substrato de óxido de estanho dopado com flúor (FTO) e após cristalização em uma estufa foi depositado um eletrodo de metal por evaporação à vácuo formando uma estrutura tipo “sanduíche”. Neste trabalho foram construídos dispositivos com eletrodo superior de Alumínio (Al) e Ouro (Au), denominados: FTO/CH/Al e FTO/CH/Au. O comportamento elétrico dos dispositivos de FTO/CH/Al foram analisados aplicando-se as teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel, o que tornou possível encontrar alguns parâmetros como: altura da barreira para a junção metal/CH, condutividade do CH e fator de retificação. O dispositivo de FTO/CH/Au foi caracterizado pela técnica de espectroscopia de impedância, sendo obtido também a altura da barreira para a junção metal/CH, a condutividade do CH, além da constante dielétrica do compósito e como variam esses dois últimos parâmetros com a temperatura. A aplicação das teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel produziram resultados semelhantes aos obtidos pela técnica de espectroscopia de impedância. Os espectros de luminescência apresentaram um pico em l = 528 nm com estabilidade temporal de emissão comparável a dos dispositivos inorgânicos puros.
Abstract (english)
In this work was developed an electroluminescent (EL) device made up with a hybrid composite (CH), that is formed by a polymeric blend and an inorganic EL material. The conductive polymer, poly(o-methoxyaniline) (POMA) doped with p-Toluene sulphonic acid (TSA), and an isolating polymer, the poly(vinylidenefluoride-co-trifluoroethylene) (P(VDFTrFE)), was used to make the polymer blend. An inorganic EL material, the zinc silicate manganese-doped (Zn2SiO4:Mn), was added to the blend, forming the hybrid composite. The composite was deposited by drop-casting over a Fluoride Tin Oxide substrate (FTO) and after the crystallization in an oven a metal electrode was deposited by vacuum evaporation, forming a type “sandwich” structure. In this work were constructed different devices. Aluminum (Al) and Gold (Au) were used as upper electrodes, therefore the device structures were: FTO/CH/Al and FTO/CH/Au. To analyze the electrical behavior of the FTO/CH/Al device was applied the theories of Thermionic Emission, Schottky Emission and Poole- Frenkel Emission. Using these theories was possible to obtain parameters such as; the barrier height from the metal/CH junction, CH conductivity and diode rectifier factor. The FTO/CH/Au device was characterized using the impedance spectroscopy technique. For this device was also possible to obtain the barrier height from the metal/CH junction, CH conductivity and CH dielectric constant. For the last two parameters the dependence with the temperature were also observed. The application of the theories of Thermionic Emission, Schottky Emission and Poole-Frenkel Emission produced similar results to that obtained by the impedance spectroscopy technique. The luminescence spectra, for the devices, showed a peak at l = 528 nm with emission stability in time that it is comparable of pure inorganic devices.
Description
Keywords
Polimeros, Espectroscopia de impedancia, Compósito (POMA/P(VDF-TrFE/Zn2SiO4:Mn), Dispositivo emissor de luz, Emissão termoiônica, Emissão Schottky, Emissão Poole-Frenkel, Light emitting device, Thermionic emission and schottky emission, Impedance Spectroscopy, Poole-frenkel emission
Language
Portuguese
Citation
STEFANELO, Josiani Cristina. Estudo das propriedades elétro-óptica de dispositivos eletroluminescentes confeccionados com um compósito híbrido. 2009. 77 f. Dissertação (mestrado) - Universidade Estadual Paulista, Instituto de Geociências e Ciências Exatas, 2009.