Y-TZP zirconia regeneration firing: Microstructural and crystallographic changes after grinding
Nenhuma Miniatura disponível
Data
2017-01-01
Autores
Ryan, Daniel Patrick Obelenis [UNESP]
Fais, Laiza Maria Grassi [UNESP]
Antonio, Selma Gutierrez [UNESP]
Hatanaka, Gabriel Rodrigues [UNESP]
Candido, Lucas Miguel [UNESP]
Pinelli, Ligia Antunes Pereira [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
This study evaluated microstructural and crystallographic phase changes after grinding (G) and regeneration firing/anneling (R) of Y-TZP ceramics. Thirty five bars (Lava™ and Ice Zirkon) were divided: Y-TZP pre-sintered, control (C), regeneration firing (R), dry grinding (DG), dry grinding+regeneration firing (DGR), wet grinding (WG) and wet grinding+regeneration firing (WGR). Grinding was conducted using a diamond bur and annealing at 1,000°C. The microstructure was analyzed by SEM and the crystalline phases by X-ray diffraction (XRD). XRD showed that pre-sintered specimens contained tetragonal and monoclinic phases, while groups C and R showed tetragonal, cubic and monoclinic phases. After grinding, the cubic phase was eliminated in all groups. Annealing (DGR and WGR) resulted in only tetragonal phase. SEM showed semi-circular cracks after grinding and homogenization of particles after annealing. After grinding, surfaces show tetragonal and monoclinic phases and R can be assumed to be necessary prior to porcelain layering when grinding is performed.
Descrição
Palavras-chave
Surface analysis, Surface treatment, XRD (X-ray diffraction), Zirconia
Como citar
Dental Materials Journal, v. 36, n. 4, p. 447-453, 2017.