Publicação: Stress distribution and failure load of multilayer and monolayer glass ceramic
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
This short report evaluated the differences in stress concentration and the load to fracture of multilayered and monolayer glass ceramic discs. Using a simulated static structural analysis, the 3D model of the samples received a load of 150 N and results in maximum principal stress were obtained. For the in vitro analysis, the samples (ø 12 mm) were submitted to a compressive test (100 kgf, 1 mm/min). The data was analyzed using one-way analysis of variance and Tukey test (α = 5%). The monolayer group showed a lower stress peak (129.24 MPa) and higher load to fracture (118.38 N) than the multilayered group with 211.04MPa and 48.34N, respectively. All samples presented catastrophic failure with its origin on the tensile surface. Therefore, the monolayer ceramic group showed superior mechanical behavior than the multilayered group.
Descrição
Palavras-chave
Ceramics, Finite element analysis, Monoblock restoration
Idioma
Inglês
Como citar
Brazilian Dental Science, v. 22, n. 1, p. 17-22, 2019.