dc.identifier.citationSILVA, Alecsandro de Moura. Influência de diferentes tratamentos de superfície em uma cerâmica policristalina de zircônia tetragonal (ytzp), na resistência de união com cimento resinoso. 2012. 116 f. Dissertação (mestrado) – UNESP - Univ Estadual Paulista,Faculdade de Odontologia de São José dos Campos, 2012.
dc.identifier.urihttp://hdl.handle.net/11449/97335
dc.description.abstractEste estudo avaliou, in vitro, a influência de diferentes tratamentos de superfície na resistência de união ao cisalhamento entre uma cerâmica de zircônia tetragonal policristalina estabilizada com ítria (Y-TZP) e um cimento resinoso. Amostras com tamanho mínimo de (1,5 X 1,5cm) uma cerâmica de Y-TZP foram confeccionados e sintetizados, de acordo com as recomendações do fabricante, e limpos sonicamente em água destilada por 10 min. De acordo com os fatores “tratamento de superfície” e “presença de filme à base de Si”, os blocos foram aleatoriamente divididos em 6 grupos: G1) polido; G2) polido revestido com filme; G3) jateamento com partículas (110μm) de alumina revestida por sílica; G4) jateamento com partículas (110 μm) de alumina revestida por sílica revestido com filme; G5) jateamento com partículas (100μm) de alumina; G6) jateamento com partículas de alumina. Os filmes foram crescidos sobre a superfície cerâmica pelo método químico de deposição a plasma utilizando o hexamethylsiloxano em forma de vapor. Cilíndros (cilíndros Ø: 2,4 mm; 4 mm altura) de um cimento resinoso (Rely X U100/3M ESPE) foram confeccionados sobre a superfície da cerâmica após o tratamento de superfície (n=10). As amostras foram submetidas ao ensaio de resistência ao cisalhamento em máquina de ensaio Universal (EMIC) a velocidade de 1 mm/min. utilizando célula de carga de 50Kgf. Os dados obtidos foram submetidos ao teste ANOVA dois fatores e ao teste Tukey com variância aceitável de 0,05%. Resultados: O estudo revelou que o filme interferiu negativamente nos resultados de resistência adesiva para a superfície jateada com óxido de alumínio e não interferiu nos resultados dos demais tratamentos de superfície Conclusão: O tratamento de superfície, com filme de plasma contendo hexamethilsiloxano em forma de...pt
dc.description.abstractThis in vitro study evaluated the influence of different surface treatments on shear bond strength between a polycrystalline ceramic tetragonal zirconia stabilized with yttria (Y-TZP) and a resin cement. Minimum number of blocks (1.5 X 1.5 cm) of a ceramic Y-TZP were prepared and synthesized according to the manufacturer's recommendations, and sonically cleaned in distilled water for 10 min. According to the factors surface treatment and presence of Si-based film, the blocks were randomly divided into six groups: G1) polished; G2) polished film-coated, G3) blasting particles (110μm) of alumina coated silica; G4) blasting particles (110 mM) of alumina-coated silica-coated film; G5) blasting particles (100μm) of alumina and G6) sandblasting with alumina particles. The films were grown on the ceramic surface by chemical method using plasma deposition hexamethylsiloxane in vapor form. Cylinders (2.4 mm x Ø 4 mm thick) of a cement (ESPE U100/3M Rely X) were prepared on the ceramic surface after the surface treatment (n = 10). The samples were submitted to shear bond strength in an universal testing machine (EMIC) at a speed of 1 mm / min. using a 50kgf load cell. The data were subjected to two-factor ANOVA and Tukey test with acceptable variance of 0.05%. Results: The study revealed that the film had a negative influence on bond strength to the surface blasted with aluminum oxide and did not interfere with the results of other surface treatments. Conclusion: The surface treatment with plasma containing hexamethylsiloxane film in vapor form (HMDSO) did not produce better bond strength values by the method of shear type knife when compared to gold standard system blasting Rocatec (3M/ESPE). The thermal cycling... (Complete abstract click electronic access below)en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent116 f. :
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (UNESP)
dc.sourceAleph
dc.subjectCimentos dentariospt
dc.subjectMateriais dentáriospt
dc.subjectCerâmica odontológicapt
dc.titleInfluência de diferentes tratamentos de superfície em uma cerâmica policristalina de zircônia tetragonal (ytzp), na resistência de união com cimento resinosopt
dc.typeDissertação de mestrado
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)
dc.rights.accessRightsAcesso aberto
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaAvaliação Clínica e Laboratorial de Materiais e Novas Tecnologias em Prótese Dentáriapt
unesp.campusUniversidade Estadual Paulista (UNESP), Instituto de Ciência e Tecnologia, São José dos Campospt
dc.identifier.aleph000706577
dc.identifier.filesilva_am_me_sjc.pdf
dc.identifier.capes33004145070P8
Localize o texto completo

Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record