Surface analysis and shear bond strength of zirconia on resin cements after non-thermal plasma treatment and/or primer application for metallic alloys
Carregando...
Arquivos
Data
2017-03-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
There is no established protocol for bonding zirconia (Y-TZP) with resin cements. Non-thermal plasma (NTP) may be an alternative for the clinical problems related to adhesion. The purpose of the present study was to characterize the surface of Y-TZP exposed to methane (CH4) NTP or coated with a layer of primer for metal alloys and the association between the two methods and to evaluate the effect of NTP treatment on bond strength between Y-TZP and two resin cements. A total of 235 Y-TZP discs (8 × 2 mm) were distributed into five groups: Co (no surface treatment), Pr (primer), NTP (methane plasma), Pr + NTP and NTP + Pr. The effect of the treatment type on the surface free energy, morphology, topography and chemical composition of the Y-TZP discs was investigated. The discs were cemented to composite resin substrates using Panavia F2.0 or RelyX U200. Shear bond strength (n = 10) analyses were performed (1 mm/min) before and after thermocycling (5–55 °C, 2000 cycles) on the bonded specimens. The data were analyzed with one and three-way ANOVAs and Bonferroni tests (α = 0.05). NTP reduced the surface energy and roughness of the Y-TZP discs. SEM-EDS and XPS analyses showed the presence of the organic thin film, which significantly improved the bond strength results when Rely X U200 was used, whereas the primer treatment was more effective with Panavia F2.0. Thermocycling significantly reduced the bond strength results of the NTP and Pr + NTP groups cemented with Rely X U200 and the Pr and NTP + Pr groups cemented with Panavia F2.0. Nonthermal plasma improves the bond strength between Rely X U200 and Y-TZP and also seems to have water-resistant behavior, whereas Panavia F2.0 showed better results when associated with primer.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Materials Science and Engineering C, v. 72, p. 284-292.