Restaurações endocrown em pré-molares: influência das paredes remanescentes da estrutura dentária e materiais restauradores na resistência à fadiga

Página do item simplificado
dc.contributor.advisorMelo, Renata Marques de Melo [Unesp]
dc.contributor.authorMohidin Demachkia, Amir
dc.contributor.coadvisorJoão Paulo Mendes Tribst
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2023-09-01T11:34:54Z
dc.date.available2023-09-01T11:34:54Z
dc.date.issued2023-06-06
dc.description.abstractEste estudo teve como objetivo avaliar o efeito da estrutura dentária remanescente e dois materiais diferentes de restauração CAD/CAM no desempenho à fadiga e no modo de falha de pré-molares tratados endodonticamente restaurados por endocrowns. Um total de 90 pré-molares superiores foram tratados endodonticamente e divididos aleatoriamente de acordo com o número de paredes axiais remanescentes, e os materiais restauradores foram divididos em 6 grupos (n = 15); quatro paredes restantes restauradas com zircônia ultratranslúcida 5Y-PSZ (grupo Fo-Z) e dissilicato de lítio (grupo Fo-L), três paredes restantes restauradas com 5Y-PSZ (grupo Th-Z) e dissilicato de lítio (grupo Th-L) e duas paredes restantes restauradas com 5Y- PSZ (grupo Tw-Z) e dissilicato de lítio (Tw-L). As restaurações foram cimentadas adesivamente e os espécimes foram submetidos a cargas de fadiga gradual em seu longo eixo (carga inicial: 200 N, frequência: 20 Hz). Uma carga incremental de 100 N por 10.000 ciclos foi aplicada com um pistão metálico de Ø 6 mm até a falha. A carga de falha por fadiga (FFL) e o número de ciclos de falha (CFF) no momento da falha foram registrados e analisados estatisticamente por ANOVA 2 fatores e teste de Kaplan-Meier (α = 0,05). Os espécimes fraturados foram examinados em estereomicroscópio em 8× e 25× e os modos de falha foram determinados como reparáveis ou catastróficos. FFL e CFF foram significativamente influenciados pelo material restaurador (p < 0,05). As restaurações de 5Y-PSZ apresentaram FFL (Fo-Z = 1487 N, Tw-Z = 1427 N, Tw-Z = 1533 N) e probabilidade de sobrevivência significativamente maiores quando comparadas com dissilicato de lítio (Fo-L = 1060 N, Th-L = 940 N, Tw-L = 1000 N). O número de paredes remanescentes não afetou o comportamento de fadiga ou modo de falha dos corpos de prova. Das restaurações de dissilicato de lítio, 51% tiveram falhas reparáveis, enquanto 95% das restaurações de zircônia ultratranslúcida 5Y-ZP tiveram falhas catastróficas. Endocrowns de zircônia apresentaram melhor desempenho em fadiga do que endocrowns de dissilicato de lítio, independentemente do número de paredes remanescentes do eixo. Endocrowns de pré-molares de dissilicato de lítio e 5Y-PSZ apresentaram maior FFL do que as cargas mastigatórias normais.pt
dc.description.abstractThis study aimed to evaluate the effect of the remaining tooth structure and two different CAD/CAM restoration materials on the fatigue performance and failure mode of endodontically treated premolars restored with endocrowns. A total of 90 maxillary premolars were endodontically treated and divided randomly according to the number of remaining axial walls, and the restorative materials were divided into 6 groups (n = 15); four remaining walls restored with ultratranslucent zirconia 5Y-PSZ (group Fo-Z) and lithium disilicate (group Fo-L), three remaining walls restored with 5Y-PSZ (group Th-Z) and lithium disilicate (Group Th-L), and two remaining walls restored with 5Y-PSZ (group Tw-Z) and lithium disilicate (Tw-L). The restorations were cemented adhesively and the specimens were subjected to stepwise fatigue loading along the long axis (initial load: 200 N, frequency: 20 Hz). An incremental step load of 100 N per 10,000 cycles was applied with a Ø6-mm metallic piston until failure. The fatigue failure load (FFL) and number of failure cycles (CFF) at the time of failure were recorded and statistically analyzed with two-way ANOVA and the Kaplan-Meier test (α = 0.05). Fractured specimens were examined under a stereomicroscope at 8× and 25× and failure modes determined as reparable or catastrophic. FFL and CFF were significantly influenced by restorative material (p < 0.05). 5Y-PSZ endocrowns showed significantly higher FFL (Fo-Z = 1487 N, Th-Z = 1427 N, Tw-Z = 1533 N) and survival probability when compared with lithium disilicate (Fo-L = 1060 N, Th-L = 940 N, Tw-L = 1000 N). The number of remaining walls did not affect the fatigue behavior or failure mode of the specimens. Of the lithium disilicate restorations, 51% had repairable failures, while 95% of ultratranslucent zirconia 5Y-ZP restorations had catastrophic failures. Zirconia endocrowns showed better fatigue performance than lithium disilicate endocrowns, regardless of the number of remaining axis walls. Lithium disilicate and 5Y-PSZ premolar endocrowns showed higher FFL than the normal masticatory loads.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipId888.595423/2020-00
dc.identifier.capes33004145070P8
dc.identifier.urihttp://hdl.handle.net/11449/250562
dc.language.isoeng
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso restrito
dc.subjectCerâmicaspt
dc.subjectCAD/CAMpt
dc.subjectFadigapt
dc.subjectFalha de restaurações dentariaspt
dc.subjectAnálise de elementos finitospt
dc.subjectCeramicsen
dc.subjectCAD/CAMen
dc.subjectFatigueen
dc.subjectDental restoration failuresen
dc.subjectFinite element analysisen
dc.titleRestaurações endocrown em pré-molares: influência das paredes remanescentes da estrutura dentária e materiais restauradores na resistência à fadigapt
dc.title.alternativeEndocrown restorations in premolars: influence of remaining axial walls of tooth structure and restorative materials on fatigue resistanceen
dc.typeTese de doutorado
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargo24 meses após a data da defesapt
unesp.examinationboard.typeBanca públicapt
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesempenho de materiais reabilitadores protéticospt

Arquivos

Pacote Original
Agora exibindo 1 - 2 de 2
Imagem de Miniatura
Nome:
demaschkia_am_dr_sjc_parc.pdf
Tamanho:
395.8 KB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Nenhuma Miniatura disponível
Nome:
demaschkia_am_dr_sjc_int.pdf
Tamanho:
1.63 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.05 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Teses - Odontologia Restauradora - ICT