Publicação: Effect of a resin-modified glass-ionomer with calcium on enamel demineralization inhibition: An in vitro study
Carregando...
Data
2019-01-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
We assessed the effect of a new coating material based on resin-modified glass-ionomer with calcium (Ca) in inhibiting the demineralization of underlying and adjacent areas surrounding caries-like lesions in enamel. The measures used were surface hardness (SH) and cross-sectional hardness (CSH). Thirty-six bovine enamel specimens (3 × 6 × 2 mm) were randomly allocated into three groups (n = 12): No treatment (NT); resin-modified glass-ionomer with Ca (Clinpro XT Varnish, 3M ESPE) (CL), and fluoride varnish (Duraphat, Colgate) (DU). The specimens were subjected to alternated immersions in demineralizing (6 h) and remineralizing solutions (18 h) for 7 days. SH measurements were conducted at standard distances of 150, 300, and 450 μm from the treatment area. CSH evaluated the mean hardness profile over the depth of the enamel surface and at standard distances from the materials. The energy-dispersive X-ray spectroscopy analysis was conducted to evaluate the demineralization bands created on the sublayer by % of calcium (Ca), phosphorus (P), and fluoride (F). Ca/P weight ratio was also calculated. Based on SH and CSH measurements, there was no difference between groups at the distances 150 μm (p = 0.882), 300 μm (p = 0.995), and 450 μm (p = 0.998). Up to 50 μm depth (at 150 μm from the treatment area), CL showed better performance than DU ( p< 0.05). NT presented higher loss of Ca and P than CL and DU (p < 0.05). There was no significant difference in the % of F ion among the three groups. The new coating material was similar to F varnish in attenuating enamel demineralization.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Brazilian Oral Research, v. 33.