Influence of boronizing treatment on Fe-Mn-Al-Si-C steel

Nenhuma Miniatura disponível

Data

2016-01-01

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Tipo

Artigo

Direito de acesso

Acesso restrito

Resumo

Austenitic Fe-Mn-Al-Si-C steel provides excellent cold formability and lower density compared to conventional stainless steels. These steels owe their corrosion and oxidation resistance to their aluminum and silicon contents, and the stability of their gamma phase is due to manganese and carbon alloying elements. The production of a boride layer with high hardness can significantly increase its surface hardness and consequently its wear resistance. In this work, Fe-31Mn-7.5Al-1.3Si-0.9C steel samples were subjected to a boriding treatment for 4 h at 900°C. The composition of the bath was 90 % borax and 10 % aluminum. Boride layers with high hardness levels were obtained (1900 HV). There was also a marked increase in wear resistance of the material.

Descrição

Idioma

Inglês

Como citar

Materials Performance and Characterization, v. 5, n. 1, p. 1-6, 2016.

Itens relacionados

Financiadores

Coleções