Solubility, porosity and fluid uptake of calcium silicate-based cements

Carregando...
Imagem de Miniatura

Data

2018-01-01

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Univ Sao Paulo Fac Odontologia Bauru

Tipo

Artigo

Direito de acesso

Acesso abertoAcesso Aberto

Resumo

Objective: To evaluate the absorption/fluid uptake, solubility and porosity of White mineral trioxide aggregate (MTA) Angelus, Biodentine (BIO), and zinc oxide-eugenol (ZOE). Material and Methods: Solubility was evaluated after immersion in distilled water for 7 and 30 days. Porosity was evaluated using digital inverted microscope, scanning electron microscope (SEM) and micro-computed tomography (micro-CT). For the fluid uptake test, specimens were immersed in Hank's balanced salt solution (HBSS) for 1, 7, 14 and 28 days. Fluid absorption, solubility and porosity of the materials were measured after each period. Statistical evaluation was performed using one-way analysis of variance (ANOVA) and Tukey tests, with a significance level at 5%. Results: After 7 and 30 days, BIO showed the highest solubility (p<0.05). All methods demonstrated that MTA had total porosity higher than BIO and ZOE (p<0.05). Micro-CT analysis showed that MTA had the highest porosity at the initial period, after its setting time (p<0.05). After 7 and 30 days, ZOE had porosity lower than MTA and BIO (p<0.05). Absorption was similar among the materials (p>0.05), and higher fluid uptake and solubility were observed for MTA in the fluid uptake test (p<0.05). Conclusions: BIO had the highest solubility in the conventional test and MTA had higher porosity and fluid uptake. ZOE had lower values of solubility, porosity and fluid uptake. Solubility, porosity and fluid uptake are related, and the tests used provided complementary data.

Descrição

Idioma

Inglês

Como citar

Journal Of Applied Oral Science. Bauru-sp: Univ Sao Paulo Fac Odontologia Bauru, v. 26, 8 p., 2018.

Itens relacionados