Análise da rota de processamento da liga Ti-30T visando a aplicação biomédica

dc.contributor.advisorClaro, Ana Paula Rosifini Alves [UNESP]
dc.contributor.advisorHein, Luiz Rogério de Oliveira [UNESP]
dc.contributor.authorKonatu, Reginaldo Toshihiro [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:27:10Z
dc.date.available2014-06-11T19:27:10Z
dc.date.issued2014-01-21
dc.description.abstractLigas de titânio são utilizadas para aplicações biomédicas devido as excelentes propriedades como a alta resistência à corrosão, biocompatibilidade e propriedades mecânicas. No presente trabalho, foram analisadas as microestruturase as propriedades mecânicas daliga Ti-30Ta e em amostras deformadas com diferentes graus de compressão. A liga foi obtida pela fusão dos metais puros em um forno a arcovoltaico com atmosfera inerte de argônio. O material obtido foi homogeneizado em um forno tubular a 1000 °C por 24 h e deformadas a friopelo processodeforjamento rotativo para obter barras de 13 mm de diâmetro. A liga foi avaliada utilizadastécnicas de difração de raios-X (DRX) em temperatura ambiente e com aquecimento, calorimetria diferencial de varredura(DSC), microscopia eletrônica de transmissão (TEM), microdureza e compressão de corpos de provas em diferentes graus de deformação. As amostras foram deformadas com taxas graus de 19%, 22% e 43% e analisadas, usando as técnicas de DRX,microscopia óptica, microdureza. A liga apresentou transformação alotrópica a uma temperatura próxima de 650°C, e microestrutura do tipo α'', a deformação da amostra resultou em cisalhamento na amostra de 43%, as amostras apresentaram microdureza de 250, 269, 286 e 280HV para as amostras sem deformação, 19%, 22%e 43% de deformaçãopt
dc.description.abstractTitanium and its alloys have been used for biomedical applications due their excellent properties, such as high corrosion resistance, biocompatibility and mechanical proprieties. In this work, the microstructure and mechanical proprieties of Ti-30Taand deformeds amples with different degrees of compression were analyzed The in gots were obtained in a arc melting furnace inan argon atmosphere. In gots were homogenized at 1000 ºCin a tubular furnace with argon atmosphere for 24 hours and than they were cold worked by swaging. and samples with 13 m mindiameter were obtained. The alloy was evaluated by X-raydiffraction (XRD), Heat treatment X ray diffraction (HTXRD)and differential scanning calorimetrical (DSC), transmission electron microscopy(TEM), micro hard nessand compression test with different deformations. The samples were forging at reductionratiosof 19%, 22% and 43%. After this deformation,its microstructure were evaluated by optical microscopy, X-ray diffraction(XRD)and micro hardness in each condition. The alloy show a allotropic transformation at 650 °C, and α'' microstructure. The sample that was compressed with 43% shear and the others samples ( 19%, 22%) don´t change their microstructure. the samples without deformation, 19%, 22% and 43% result 250, 269, 286, 280 HVen
dc.format.extent59 f. : il.
dc.identifier.aleph000734240
dc.identifier.capes33004080027P6
dc.identifier.citationKONATU, Reginaldo Toshihiro. Análise da rota de processamento da liga Ti-30T visando a aplicação biomédica. 2014. 59 f. Dissertação (mestrado) - Universidade Estadual Paulista. Faculdade de Engenharia de Guaratinguetá, 2014.
dc.identifier.file000734240.pdf
dc.identifier.lattes2302418953025459
dc.identifier.lattes0778348300548797
dc.identifier.urihttp://hdl.handle.net/11449/94376
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectLigas de titaniopt
dc.subjectMicroestruturapt
dc.subjectMateriais biomédicospt
dc.subjectRaios X - Difraçãopt
dc.subjectMicroscopia eletronicapt
dc.subjectFotoelasticidadept
dc.subjectTitanium alloyspt
dc.titleAnálise da rota de processamento da liga Ti-30T visando a aplicação biomédicapt
dc.typeDissertação de mestrado
unesp.advisor.lattes2302418953025459[1]
unesp.advisor.orcid0000-0003-3353-4247[1]
unesp.author.lattes0778348300548797
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Engenharia, Guaratinguetápt
unesp.graduateProgramEngenharia Mecânica - FEGpt
unesp.knowledgeAreaMateriaispt
unesp.researchAreaBiomateriaispt

Arquivos

Pacote Original

Agora exibindo 1 - 1 de 1
Carregando...
Imagem de Miniatura
Nome:
000734240.pdf
Tamanho:
3.34 MB
Formato:
Adobe Portable Document Format