Resistência à fadiga cíclica de estruturas cerâmicas multilayers em modelos tradicionais e bioinspirados

Página do item simplificado
dc.contributor.advisorMarinho, Renata Marques de Melo [Unesp]
dc.contributor.authorContreras, Lisseth Patricia Claudio [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2021-12-15T15:05:35Z
dc.date.available2021-12-15T15:05:35Z
dc.date.issued2021-10-05
dc.description.abstractEste estudo avaliou a resistência à fadiga cíclica de estruturas em forma de disco cerâmico multicamada de configuração tradicional (T) e bionispirado em macroescala (B), cimentadas de forma adesiva ao substrato analógo à dentina. As amostras foram produzidas com zircônia (Ø = 10 mm, espessura = 0,5 mm) e cerâmica feldspática (Ø = 10 mm, espessura = 1,5 mm) e foram unidas com três técnicas diferentes (n = 15): Injeção (inj); com vidro de fusão Crystal Connect (cv) e técnica cimentada (cim). Para a configuração tradicional a zircônia foi a infraestrura sobre qual a cerâmica feldspática foi aderida. Para os bioinspirados, a zircônia foi a supraestrutura e a cerâmica feldspática foi a infraestrutura. Os discos foram cimentados em resina G-10 (Ø = 10 mm, espessura = 1,5 mm). As amostras foram testadas sob a abordagem de fadiga cíclica até apresentar alguma trinca observada por transluminação. O método stepwise: 20 Hz, seguidos por etapas incrementais de 200 N a cada 10 x 103ciclos, com carga inicial de 600 N até 2600 N com pistão de 40 mm de diâmetro e célula de carga de 5 KN (Instron Electropuls E 3000, Instron, Glenview, IL, EUA). Todas as amostras foram analisadas estereomicroscópio para determinar o tipo de falha e uma amostra representativa de cada grupo foi analisada no microscópio eletrônico de varredura (MEV). As configurações bioinspiradas testadas foram estatisticamente semelhantes (p > 0,05) e não aumentaram a sobrevivência à fadiga das estruturas comparadas com a técnica tradicional. A bioinspiração apresentou predominantemente trincas radias e únicas. A gradação do modulo elástico em macroescala e a configuração das estruturas. A utilização do conector vítreo se mostro favorável para diminuir das trincas no material análogo á dentina.pt
dc.description.abstractThis study evaluated the cyclic fatigue resistance of multilayer ceramic discshaped structures of traditional configuration (T) and macroscale bionispirate (B), cemented adhesively to the substrate analogic to dentin. The samples were produced with zirconia (Ø = 10 mm, thickness = 0.5 mm) and feldspar ceramics (Ø = 10 mm, thickness = 1.5 mm) and were joined with three different techniques (n = 15): Injection (inj); with Crystal Connect melting glass (cv) and cemented technique (Cim). For the traditional configuration zirconia was the infraestrura on which the feldspathic ceramic was adhered. For the bioinspired, zirconia was the superstructure, and feldspathic ceramics was the infrastructure. The discs were cemented in G-10 resin (Ø = 10 mm, thickness = 1.5 mm). The samples were tested under the cyclic fatigue approach until some crack was observed by translumination. The stepwise method: 20 Hz, followed by incremental steps of 200 N every 10 x 103 cycles, with initial charge from 600 N to 2600 N (40 mm diameter piston) and 5 KN load cell (Instron Electropuls E 3000, Instron, Glenview, IL, USA). All samples were analyzed stereomicroscopically to determine the type of failure and a representative sample of each group was analyzed in the scanning electron microscope (SEM). The bioinspired configurations tested were statistically similar (p > 0.05) and did not increase the fatigue survival of the structures compared to the traditional technique. The bioinspiration presented predominantly radial and unique cracks. The use of the vitreous connector was favorable to decrease the cracks in the analogous dentin material.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipId88882.434266/2018-01
dc.identifier.capes33004145070P8
dc.identifier.urihttp://hdl.handle.net/11449/215470
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subjectPrótese dentalpt
dc.subjectPorcelanapt
dc.subjectZircôniapt
dc.subjectBioinspiraçãopt
dc.subjectDental prosthesisen
dc.subjectPorcelainen
dc.subjectZirconiaen
dc.subjectBioinspirationen
dc.titleResistência à fadiga cíclica de estruturas cerâmicas multilayers em modelos tradicionais e bioinspiradospt
dc.title.alternativeCyclic fatigue resistance of multilayer ceramic structures in traditional and bioinspired modelsen
dc.typeTese de doutorado
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargoOnlinept
unesp.examinationboard.typeBanca públicapt
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesempenho de Materiais Reabilitadorespt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
contreras_lpc_dr_sjc.pdf
Tamanho:
13.37 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.01 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Teses - Odontologia Restauradora - ICT