Effect of finishing/polishing techniques and low temperature degradation on the surface topography, phase transformation and flexural strength of ultra-translucent ZrO2 ceramic

Nenhuma Miniatura disponível

Data

2020-04-01

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Tipo

Artigo

Direito de acesso

Resumo

Objective: To investigate the effect of different surface finishing and polishing regimes and low temperature degradation on flexural strength, phase transformation and surface topography of ultra-translucent ZrO2 ceramic. Methods: 300 (n = 15/group) of conventional zirconia (Z: Ice Zirkon Transluzent) and ultra-translucent zirconia (UT: Prettau Anterior) bar-specimens were made and divided according to the “Finishing/Polishing” - (C — Control, B — diamond rubber polishers, P — adjusting with burs, PB — adjusting with burs + diamond polishers, PG — adjusting with burs + glaze), “Low temperature Degradation (LTD)” (with or without a treatment at 127 °C, 1.7 bar/24 h). Then, a 3-point mini flexural test was performed in a universal testing machine (1 mm/min, 500 kgf load cell). SEM, EDS, XDR, AFM, optical profilometry and Weibull analysis were performed. Data were analyzed by 3-way ANOVA and Tukey's post-test (5%). Results: Groups ZPBD (1670 ± 253 MPa), ZBD (1664 ± 217 MPa), and ZB (1655 ± 3678 MPa) showed significantly higher flexural strength than the UTPG group (372 ± 56 MPa). The Weibull modulus was significantly higher for the ZPD group compared to the UB, UCD, UPD and UPBD, while UTB, UTCD and UTPD had the lowest value. Monoclinic phases were observed only in the conventional zirconia groups and were more evident after LTD. Diamond rubber polishers presented less roughness for both zirconias. Significance: The use of diamond rubber polishers is the most suitable finishing/polishing method for zirconia ceramic restorations and that final glazing reduces the fracture resistance of these materials.

Descrição

Idioma

Inglês

Como citar

Dental Materials, v. 36, n. 4, p. e126-e139, 2020.