Efeito do envelhecimento nas propriedades de um cimento de ionômero de vidro modificado por nanopartículas de hidroxiapatita ou por vidros bioativos 45S5

dc.contributor.advisorZuanon, Angela Cristina Cilense [UNESP]
dc.contributor.authorMartins, Rafael Amorim
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2022-04-11T11:31:39Z
dc.date.available2022-04-11T11:31:39Z
dc.date.issued2022-03-04
dc.description.abstractOs cimentos de ionômero de vidro (CIV) possuem características importantes, as quais podem ser potencializadas a partir de sua associação às nanopartículas (NP) e aos vidros bioativos (VB). Considerando possíveis alterações que esta associação pode ocasionar no material restaurador em curto e em longo prazo, o objetivo deste estudo foi avaliar, antes e após envelhecimento (termociclagem após seis meses de armazenamento), propriedades físicas, mecânicas e microbiológicas de um CIV convencional (Controle) associado a 5% de NP de hidroxiapatita (NPHPa) ou a 5% de VB 45S5 (VB). A atividade antibiofilme foi definida pela contagem de unidades formadoras de colônia (UFC/ml) em 1, 7, 14 e 21 dias. A rugosidade de superfície foi estudada com auxílio de rugosímetro. Espectrofotômetro auxiliou na análise de estabilidade de cor (∆E e sistema CIELab). A porosidade foi analisada por meio do programa Image J, a partir de imagens obtidas por MEV. Dureza Vickers foi analisada por meio de microdurômetro digital. Foram realizadas também imagens em MEV e EDS para análise qualitativa e caracterização da morfologia e composição química superficial. A normalidade dos dados foi observada para todos os testes a partir da análise de Shapiro-Wilk seguido de ANOVA two-way. Para ∆E foi realizado Kruskal-Wallis. Nível de significância de 5% foi utilizado para todos os testes. Pôde-se observar diminuição de UFC/ml para todos os grupos em 14 dias antes e após envelhecimento. Inicialmente valores menores de rugosidade foram encontrados para VB, enquanto valores semelhantes foram encontrados para todos os grupos após envelhecimento. Menores valores de luminância foram encontrados para os grupos NPHPa e VB, com ∆E sem diferenças estatísticas. Quanto a porosidade, após envelhecimento, maior número de poros apresentou NPHPa embora tenha demonstrado menor área total. A dureza do Controle e NPHPa apresentou aumento dos valores após envelhecimento, tendo NPHPa os maiores. Diminuição desses valores foi observado em VB, o qual resultou em menor dureza ao final do estudo. Conclui-se que a associação do CIV a NPHPa é mais promissora e pode trazer benefícios a longo prazo.pt
dc.description.abstractGlass ionomer cements (GIC) have important characteristics, which can be enhanced by their association with nanoparticles (NP) and bioactive glasses (BAG). Considering the possible changes that this association can cause in the restorative material in the short and long term, the aim of this study was to evaluate, before and after aging (thermocycling after six months of storage), physical, mechanical and microbiological properties of a conventional GIC (Control) associated with 5% hydroxyapatite NP (NPHPa) or 5% BAG 45S5 (BAG). Antibiofilm activity was defined by counting colony forming units (CFU/ml) at 1, 7, 14 and 21 days. Surface roughness was studied with the aid of a rugosimeter. Spectrophotometer assisted in the analysis of color stability (∆E and CIELab system). Porosity was analyzed using the Image J program, from images obtained by SEM. Vickers hardness was analyzed using a digital microhardness meter. SEM and EDS images were also taken for qualitative analysis and characterization of morphology and surface chemical composition. Data normality was observed for all tests from the Shapiro-Wilk analysis followed by ANOVA two-way. For ∆E was performed Kruskal-Wallis. A 5% significance level was used for all tests. It was possible to observe a decrease in CFU/ml for all groups in 14 days before and after aging. Initially, lower roughness values were found for BAG, while similar values were found for all groups after aging. Lower luminance values were found for groups NPHPa and BAG, with ∆E without statistical differences. As for porosity, after aging, a greater number of pores presented NPHPa although it showed a smaller total area. The hardness of Control and NPHPa showed an increase in values after aging, with NPHPa being the highest. A decrease in these values was observed in BAG, which resulted in lower hardness at the end of the study. It is concluded that the association of GIC with NPHPa is more promising and may bring long-term benefits.pt
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.description.sponsorshipIdCapes: 001
dc.identifier.capes33004030010P2
dc.identifier.urihttp://hdl.handle.net/11449/217726
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso restrito
dc.subjectCimentos de ionômeros de vidropt
dc.subjectNanopartículaspt
dc.subjectEnvelhecimentopt
dc.subjectGlass ionomer cementsen
dc.subjectNanoparticlesen
dc.subjectAgingen
dc.titleEfeito do envelhecimento nas propriedades de um cimento de ionômero de vidro modificado por nanopartículas de hidroxiapatita ou por vidros bioativos 45S5pt
dc.title.alternativeAging effect on the properties of a glass ionomer cement modified by hydroxyapatite nanoparticles or by 45S5 bioactive glassesen
dc.typeTese de doutorado
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Odontologia, Araraquarapt
unesp.embargo24 meses após a data da defesapt
unesp.examinationboard.typeBanca públicapt
unesp.graduateProgramCiências Odontológicas - FOARpt
unesp.knowledgeAreaOdontopediatriapt
unesp.researchAreaAvaliação das propriedades químicas, físicas, mecânicas e biológicas de materiais dentáriospt

Arquivos

Pacote Original

Agora exibindo 1 - 2 de 2
Carregando...
Imagem de Miniatura
Nome:
martins_ra_dr_arafo_par.pdf
Tamanho:
368.5 KB
Formato:
Adobe Portable Document Format
Descrição:
Carregando...
Imagem de Miniatura
Nome:
martins_ra_dr_arafo_int.pdf
Tamanho:
620.15 KB
Formato:
Adobe Portable Document Format
Descrição:

Licença do Pacote

Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.04 KB
Formato:
Item-specific license agreed upon to submission
Descrição: